Eurostar Starpylen MF008S PP, 40% Glass Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starpylen |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starpylen MF008S PP, 40% Glass Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starpylen MF008S is a 40% Glass Fiber Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| Flexural Strength | 129 MPa | 18700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80x10x4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | HB | HB | 1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 195 - 205 °C | 383 - 401 °F | |
| Zone 2 | 215 - 225 °C | 419 - 437 °F | |
| Zone 3 | 225 - 250 °C | 437 - 482 °F | |
| Melt Temperature | 225 - 250 °C | 437 - 482 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- Polystrand ThermoPro™ IE6010 Unitape Unidirectional Polypropylene-Glass Composite
- SABIC Innovative Plastics LNP COLORCOMP EX10304C PEI (Asia Pacific)
- LG Chemical BPA
- SGL Carbon Group PANOX® SA T320 EEA High performance oxidized textile fiber, Continuous Tow with 320k filaments
- SABIC Innovative Plastics Valox® DR51M PBT (Asia Pacific)
- Spartech DP5120 Talc Filled Homopolymer
- C.O.I.M. FILCO® 309 Film Former for Glass Fiber Sizes
- Braskem TI60035NB High Impact Copolymer Polypropylene
- 3M Scotchfil™ Electrical Insulation Putty
- Loctite® Gasket Eliminator® 510 Flange Sealant
Copyright © lookpolymers.com All Rights Reserved