Eurostar Starflam UF0033 PPA, Glass Fiber Filled, Flame Retardant, Injection Molded
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 10% Glass Fiber Reinforced |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam UF0033 PPA, Glass Fiber Filled, Flame Retardant, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam UF0033 is a Mineral Flame Retardant, Halogen Free and Red Phosphorous Free, Glass Reinforced, Polyphthalamide Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | janv, 5 mm/min; ISO 527 |
| Flexural Strength | 140 MPa | 20300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 9.90 GPa | 1440 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80x10x4; ISO 179/1eA |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 280 - 300 °C | 536 - 572 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 295 - 315 °C | 563 - 599 °F | |
| Melt Temperature | 305 - 315 °C | 581 - 599 °F | |
| Mold Temperature | 130 - 150 °C | 266 - 302 °F | |
| Drying Temperature | 120 - 140 °C @Time 14400 - 21600 sec |
248 - 284 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | >= 0.10 % | >= 0.10 % |
Users viewing this material also viewed the following:
- Potters Industries Q-Cel® 7028 Hollow Engineered Glass Microspheres
- LATI Latilub 87/28-12T G/20 PC, 20% Glass Fiber Reinforced, PTFE Filled
- Borealis BorPURE™ RE216CF Polypropylene Random Copolymer
- Wieland 1023 Wilaform Gold
- A. Schulman POLYBATCH™ Lattice Grey 80354U/4 Concentrate Based In LLDPE
- DuPont Teijin Films Melinex® 339 Polyester Film, 700 Gauge
- ChevronTexaco Delo® 1000 Marine Engine Oil, SAE 50
- Ametek High Purity Nickel Strip 899M Annealed
- Arlon 55106R030 0.030" (0.762 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Overview of materials for Acrylic, Impact Modified, Molded
Copyright © lookpolymers.com All Rights Reserved