Eurostar Starflam PX05003 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam PX05003 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam PX05003 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 4.00 mm |
0.0040 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 91.0 MPa | 13200 psi | ISO 527 |
| Elongation at Break | 2.4 % | 2.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 0.620 GPa | 89.9 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 140 MPa | 20300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.70 GPa | 827 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 500 V | 500 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Precision Polymer Engineering F50A Fluorosilicone Rubber
- PolyMirae Moplen RP370G Blow Molding Grade Polypropylene
- Resistalloy International Fecralloy™ 145 Electrical Resistance Steel
- Rotuba MS Cellulose Acetate
- Hyosung Topilene R301 PP
- Techmer ES HiFill® PA6/6 0249 B Nylon 66
- Techmer ES Luriblend® PA6/6 GF33 TS15 BK 33% Glass Filled
- Teknor Apex Telcar® TL-2433A Thermoplastic Elastomer
- ExxonMobil EXACT™ 3128 Plastomer for Blown Film Applications
- Braskem CP360H Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved