Eurostar Starflam PK00032E PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Mineral Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam PK00032E PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam PK0032E is a Halogen Free Red Phosphorous Free Flame Retardant Mineral Filled Reinforced Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| Water Absorption | 1.6 % @Temperature 23.0 °C, Time 86400 sec |
1.6 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 4.00 mm |
0.0080 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 67.0 MPa | 9720 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.2 % | 3.2 % | 5 mm/min; ISO 527 |
| 6.6 % | 6.6 % | Flexural, 2 mm/min; ISO 178 | |
| Elongation at Yield | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.70 GPa | 682 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 101 MPa | 14600 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 107 MPa | 15500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.10 GPa | 595 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C | 163 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 20 Polyamide 6, 20% Glass Fiber
- PolyOne Edgetek® ATH-20CF/000 Acetal-Homopolymer, Carbon Fiber Reinforced (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP ABL12 ABS
- Ineos Nova 1300 High Heat Crystal Polystyrene
- Solvay ALKAMULS® R 81 Surfactant
- Unitika elitel UE9600 Polyester, Pellet
- A. Schulman POLYBATCH™ Green 3315 Concentrate Based In Polyethylene
- BASF Pluracol® GP 430R Specialty Polyol
Copyright © lookpolymers.com All Rights Reserved