Eurostar Starflam P10003 PA6, Mineral Filled, Flame Retardant, Extrusion
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam P10003 PA6, Mineral Filled, Flame Retardant, Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam P10003 is a Mineral Filled, Halogen Free, Red Phosphorous Free, Flame Retardant, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Water Absorption | 0.90 % @Temperature 23.0 °C, Time 86400 sec |
0.90 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 4.00 mm |
0.010 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| 4.5 % | 4.5 % | Flexural, 2 mm/min; ISO 178 | |
| Tensile Modulus | 6.70 GPa | 972 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 122 MPa | 17700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.20 GPa | 899 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
35.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 77.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
42.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 245 - 255 °C | 473 - 491 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 255 - 265 °C | 491 - 509 °F | |
| Mold Temperature | 55.0 - 95.0 °C | 131 - 203 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 9402-SR BLK
- Polykemi AB POLYfill PP CQX8025 R2 Polypropylene, Mineral Reinforced, Scratch Resistant
- Niche Polymer PPCG40BK Copolymer PP, 40% Glass Fiber Filled
- PolyOne Geon™ Vinyl Flexible C90UB Polyvinyl Chloride, Flexible (PVC, Flexible)
- McDanel Advanced Ceramics AP 35 99% Alumina
- Special Metals INCOLOY® 25-6M0 Super Austenitic Stainless Steel (UNS N08926)
- Techmer ES HiFill® TPX-HTN-01036 A 30% Mineral Filled
- Elektro-Isola Etronit IS Phenolic, Paper Reinforcement, Dark Brown, Sheets
- Eurostar Starflam PX06091 PA6, Flame Retardant, Injection Molded
Copyright © lookpolymers.com All Rights Reserved