DSM Arnite® TV4 220 PBT-10% Glass Reinforced (European and Asian Grade)

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
Manufacturer	DSM Engineering Plastics
Trade Name	Arnite®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DSM Arnite® TV4 220 PBT-10% Glass Reinforced (European and Asian Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame retardant gradesEasy molding FR grades for connectorsToughened unfilled materials for durabilityHigh modulus, tight specification for critical auto componentsToughened reinforced resinsLow outgassing grades for reflector surfacesArnite extrusion resins: Specialized materials for specific usesPET for medical applicationsLoose buffer Optical fiber tubingPET for stock shapesApplicationsAutomotive:Connectors, sensors and E&E parts, Exterior fittings, Gear housings and motors, Brake valve bodiesElectrical & Electronic: Telecoms and IT connectors, Bobbins, Low voltage Power distribution, E-motor components, Lightings and Lamp fittingsConsumer Durables: Small AppliancesOther: Optical fiber tubingInformation provided by DSM.

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	ISO 1183
Water Absorption	0.35 %	0.35 %	Sim. to ISO 62
Moisture Absorption at Equilibrium	0.16 %	0.16 %	Humidity Absorption; Sim. to ISO 62
Melt Flow	28.77 g/10 min @Load 2.16 kg, Temperature 250 °C	28.77 g/10 min @Load 4.76 lb, Temperature 482 °F	Calculated from Volume Flow Rate of 21 cm<sup>3</sup>/10min.; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	80.0 MPa	11600 psi	ISO 527-1/-2
Elongation at Break	5.0 %	5.0 %	ISO 527-1/-2
Tensile Modulus	4.50 GPa	653 ksi	ISO 527-1/-2
Charpy Impact Unnotched	3.00 J/cm² @Temperature -30.0 °C	14.3 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	3.00 J/cm² @Temperature 23.0 °C	14.3 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.700 J/cm² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.700 J/cm² @Temperature 23.0 °C	3.33 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	225 °C	437 °F	10°C/min; ISO 11357-1/-3
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093

Descriptive Properties	Value	Comments
Injection molding	Yes
Release Agent	Yes
With Fillers	Yes