Eurostar Staramide PK005EI2 PA6, Mineral Fiber Filled, Impact Modified Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Mineral Reinforced, Impact Grade |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide PK005EI2 PA6, Mineral Fiber Filled, Impact Modified Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide PK005EI2 is an Impact Modified Mineral Filled Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 4.00 mm |
0.0060 - 0.0080 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| Elongation at Break | >= 8.0 % | >= 8.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.60 GPa | 522 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.60 GPa | 522 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- LATI Latene® 7H2W T-V0 PP Homopolymer, Mineral Reinforced, Heat Stabilized, Flame Retardant
- Saint-Gobain CHR® SG55-06(R) Anti-Static Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Universal Wire Works 6Al-4V (ELI) (AMS 4956) Titanium Alloy Filler Metal
- Wanhua Chemical Wanthane® WHT-8185 Polyether-Based TPU
- DSM EcoPaXX® Q-PG6 PA410-I-GF30
- Ensinger Tecapeek® XP-92 Compression Molded PEEK Compound, 15% Fiberglass
- ExxonMobil 426 Mobilmet 400 Series
- Eurostar Starflam PX06012 PA6, Flame Retardant, Injection Molded
- Bulk Molding Compounds BMC T10(14) General Purpose Molding Compound
- Huntsman PE2049 Injection Molding Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved