Eurostar Staramide P1000IX2 PA6, Impact Modified, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide P1000IX2 PA6, Impact Modified, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide P1000IX2 is an Impact Modified, Polyamide 6 Injection Molding Resin (also known as P1000HI010 or Star X 2010)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.014 - 0.016 cm/cm @Thickness 4.00 mm |
0.014 - 0.016 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ISO 527 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527 |
| Elongation at Break | 80 % | 80 % | ISO 527 |
| Flexural Strength | 77.0 MPa | 11200 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1U |
| >= 100 kJ/m² @Temperature 23.0 °C |
>= 47.6 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1U | |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU |
| >= 10.0 J/cm² @Temperature 23.0 °C |
>= 47.6 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU | |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| 1.70 J/cm² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 220 - 230 °C | 428 - 446 °F | |
| Zone 2 | 230 - 240 °C | 446 - 464 °F | |
| Zone 3 | 240 - 250 °C | 464 - 482 °F | |
| Melt Temperature | 240 - 250 °C | 464 - 482 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF5015 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Hybrid Plastics Fireban® Mark VI Resorcinolinic (PRF)
- Mar-Bal MB2000-20 Thermoset Polyester Composite Molding Compound
- Solvay ALKAMULS® 14/R Surfactant
- ChevronTexaco Starplex® Moly MPGM 2
- Donnelly Bros HT 500 High Temperature Mold Grease
- Arkema Group Pebax® 7033 SN 01 Polyether Block Amide (PEBA) (Conditioned)
- BASF Ultramid® B3ZG6 BK 30564 30% Glass Filled PA6-1 (Conditioned)
- 3M Dyneon™ PVDF 11008/0003 Polyvinylidene Fluoride
Copyright © lookpolymers.com All Rights Reserved