Eurostar Staramide ALY430A PA66, Glass Fiber Reinforced, Injection Molding

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide ALY430A PA66, Glass Fiber Reinforced, Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Staramide ALY430A is a Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
on Tensile Bar; E2P method
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
5 mm/min; ISO 527
Elongation at Break 5.0 %
5.0 %
5 mm/min; ISO 527
Tensile Modulus 4.80 GPa
696 ksi
1 mm/min; ISO 527
Flexural Strength 150 MPa
21800 psi
2 mm/min; ISO 178
Flexural Modulus 4.50 GPa
653 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -40.0 °C
 2.38 ft-lb/in²

@Temperature -40.0 °F
 80x10x4; ISO 180/1A
6.00 kJ/m²

@Temperature -20.0 °C
 2.86 ft-lb/in²

@Temperature -4.00 °F
 80x10x4; ISO 180/1A
8.00 kJ/m²

@Temperature 23.0 °C
 3.81 ft-lb/in²

@Temperature 73.4 °F
 80x10x4; ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 33.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 18.3 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 92.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 51.1 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 235 °C
455 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point 245 °C
473 °F
B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Processing Properties Metric English Comments
Processing Temperature 60.0 - 80.0 °C
140 - 176 °F
Hopper
Zone 1 260 - 280 °C
500 - 536 °F
Zone 2 260 - 280 °C
500 - 536 °F
Zone 3 260 - 280 °C
500 - 536 °F
Melt Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 75.0 - 85.0 °C

@Time 14400 - 21600 sec
 167 - 185 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %