Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F)

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include afterburner parts and nozzle diaphragm partitions in current gas turbine engines. Formed with success on drop-hammers, expanding mandrels and stretch formers.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.25 g/cc
0.298 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1047 MPa
151900 psi
179 MPa

@Temperature 982 °C
 26000 psi

@Temperature 1800 °F
677 MPa

@Temperature 871 °C
 98200 psi

@Temperature 1600 °F
858 MPa

@Temperature 760 °C
 124000 psi

@Temperature 1400 °F
958 MPa

@Temperature 538 °C
 139000 psi

@Temperature 1000 °F
970 MPa

@Temperature 649 °C
 141000 psi

@Temperature 1200 °F
Tensile Strength, Yield 799 MPa

@Strain 0.200 %
 116000 psi

@Strain 0.200 %
80.0 MPa

@Strain 0.200 %,
Temperature 982 °C
 11600 psi

@Strain 0.200 %,
Temperature 1800 °F
450 MPa

@Strain 0.200 %,
Temperature 871 °C
 65300 psi

@Strain 0.200 %,
Temperature 1600 °F
535 MPa

@Strain 0.200 %,
Temperature 760 °C
 77600 psi

@Strain 0.200 %,
Temperature 1400 °F
746 MPa

@Strain 0.200 %,
Temperature 538 °C
 108000 psi

@Strain 0.200 %,
Temperature 1000 °F
748 MPa

@Strain 0.200 %,
Temperature 649 °C
 108000 psi

@Strain 0.200 %,
Temperature 1200 °F
Modulus of Elasticity 150 GPa

@Temperature 927 °C
 21800 ksi

@Temperature 1700 °F
160 GPa

@Temperature 871 °C
 23200 ksi

@Temperature 1600 °F
163 GPa

@Temperature 843 °C
 23600 ksi

@Temperature 1550 °F
166 GPa

@Temperature 816 °C
 24100 ksi

@Temperature 1500 °F
171 GPa

@Temperature 760 °C
 24800 ksi

@Temperature 1400 °F
178 GPa

@Temperature 677 °C
 25800 ksi

@Temperature 1250 °F
179 GPa

@Temperature 649 °C
 26000 ksi

@Temperature 1200 °F
182 GPa

@Temperature 593 °C
 26400 ksi

@Temperature 1100 °F
188 GPa

@Temperature 538 °C
 27300 ksi

@Temperature 1000 °F
190 GPa

@Temperature 482 °C
 27600 ksi

@Temperature 900 °F
198 GPa

@Temperature 371 °C
 28700 ksi

@Temperature 700 °F
204 GPa

@Temperature 260 °C
 29600 ksi

@Temperature 500 °F
213 GPa

@Temperature 149 °C
 30900 ksi

@Temperature 300 °F
218 GPa

@Temperature 25.0 °C
 31600 ksi

@Temperature 77.0 °F
Poissons Ratio 0.31
0.31
27°C (80°F)
0.31

@Temperature 149 °C
 0.31

@Temperature 300 °F
0.32

@Temperature 482 °C
 0.32

@Temperature 900 °F
0.32

@Temperature 371 °C
 0.32

@Temperature 700 °F
0.32

@Temperature 260 °C
 0.32

@Temperature 500 °F
0.33

@Temperature 760 °C
 0.33

@Temperature 1400 °F
0.33

@Temperature 677 °C
 0.33

@Temperature 1250 °F
0.33

@Temperature 649 °C
 0.33

@Temperature 1200 °F
0.34

@Temperature 843 °C
 0.34

@Temperature 1550 °F
0.35

@Temperature 927 °C
 0.35

@Temperature 1700 °F
Shear Modulus 83.0 GPa
12000 ksi
27°C
55.0 GPa

@Temperature 927 °C
 7980 ksi

@Temperature 1700 °F
61.0 GPa

@Temperature 843 °C
 8850 ksi

@Temperature 1550 °F
64.0 GPa

@Temperature 760 °C
 9280 ksi

@Temperature 1400 °F
67.0 GPa

@Temperature 677 °C
 9720 ksi

@Temperature 1250 °F
69.0 GPa

@Temperature 593 °C
 10000 ksi

@Temperature 1100 °F
72.0 GPa

@Temperature 482 °C
 10400 ksi

@Temperature 900 °F
75.0 GPa

@Temperature 371 °C
 10900 ksi

@Temperature 700 °F
77.0 GPa

@Temperature 260 °C
 11200 ksi

@Temperature 500 °F
81.0 GPa

@Temperature 149 °C
 11700 ksi

@Temperature 300 °F
Thermal Properties Metric English Comments
CTE, linear 13.5 µm/m-°C

@Temperature 21.0 - 538 °C
 7.50 µin/in-°F

@Temperature 69.8 - 1000 °F
14.0 µm/m-°C

@Temperature 21.0 - 649 °C
 7.78 µin/in-°F

@Temperature 69.8 - 1200 °F
14.8 µm/m-°C

@Temperature 21.0 - 760 °C
 8.22 µin/in-°F

@Temperature 69.8 - 1400 °F
15.2 µm/m-°C

@Temperature 21.0 - 871 °C
 8.44 µin/in-°F

@Temperature 69.8 - 1600 °F
16.3 µm/m-°C

@Temperature 21.0 - 927 °C
 9.06 µin/in-°F

@Temperature 69.8 - 1700 °F
16.8 µm/m-°C

@Temperature 21.0 - 982 °C
 9.33 µin/in-°F

@Temperature 69.8 - 1800 °F
Specific Heat Capacity 0.452 J/g-°C

@Temperature 21.0 °C
 0.108 BTU/lb-°F

@Temperature 69.8 °F
Thermal Conductivity 11.5 W/m-K

@Temperature 149 °C
 79.8 BTU-in/hr-ft²-°F

@Temperature 300 °F
12.5 W/m-K

@Temperature 204 °C
 86.8 BTU-in/hr-ft²-°F

@Temperature 399 °F
13.6 W/m-K

@Temperature 260 °C
 94.4 BTU-in/hr-ft²-°F

@Temperature 500 °F
14.7 W/m-K

@Temperature 316 °C
 102 BTU-in/hr-ft²-°F

@Temperature 601 °F
16.8 W/m-K

@Temperature 427 °C
 117 BTU-in/hr-ft²-°F

@Temperature 801 °F
18.8 W/m-K

@Temperature 538 °C
 130 BTU-in/hr-ft²-°F

@Temperature 1000 °F
20.0 W/m-K

@Temperature 593 °C
 139 BTU-in/hr-ft²-°F

@Temperature 1100 °F
21.0 W/m-K

@Temperature 644 °C
 146 BTU-in/hr-ft²-°F

@Temperature 1190 °F
22.0 W/m-K

@Temperature 704 °C
 153 BTU-in/hr-ft²-°F

@Temperature 1300 °F
23.1 W/m-K

@Temperature 760 °C
 160 BTU-in/hr-ft²-°F

@Temperature 1400 °F
24.1 W/m-K

@Temperature 816 °C
 167 BTU-in/hr-ft²-°F

@Temperature 1500 °F
25.1 W/m-K

@Temperature 871 °C
 174 BTU-in/hr-ft²-°F

@Temperature 1600 °F
Melting Point 1310 - 1345 °C
2390 - 2453 °F
Solidus 1310 °C
2390 °F
Electrical Properties Metric English Comments
Magnetic Permeability <= 1.002

@Temperature 21.0 °C
 <= 1.002

@Temperature 69.8 °F
 200 Oersted