Arlon 30400R060 0.06" Uncured, Unsupported Silicone Rubber on Release Carrier

Category Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 30400R060 0.06" Uncured, Unsupported Silicone Rubber on Release Carrier.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Side 1: Uncured, Unsupported Silicone RubberSubstrate: Kodacel CarrierInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
Physical Properties Metric English Comments
Thickness 127 microns
5.00 mil
Substrate
1520 microns
60.0 mil
Rubber
Mechanical Properties Metric English Comments
Hardness, Shore A 55
55
Silicone Property
Tensile Strength 6.21 - 7.58 MPa
900 - 1100 psi
Silicone Property
Elongation at Break 450 - 550 %
450 - 550 %
Silicone Property
Tear Strength >= 35.1 kN/m
>= 200 pli
Silicone Property
Compression Set <= 28 %
<= 28 %
After Post-cure; Silicone Property
Thermal Properties Metric English Comments
Maximum Service Temperature, Inert 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Electrical Properties Metric English Comments
Dielectric Strength >= 15.7 kV/mm
>= 400 kV/in
Processing Properties Metric English Comments
Cure Time 30.0 min

@Temperature 177 °C
0.500 hour

@Temperature 350 °F
Recommended Cure Cycle
240 min

@Temperature 204 °C
4.00 hour

@Temperature 400 °F
Recommended Post Cure Cycle - After 30 minute ramp up cycle
Shelf Life 3.00 Month

@Temperature 4.44 °C
3.00 Month

@Temperature 40.0 °F
Descriptive Properties Value Comments
Color Clear
Kodacel
Red
Silicone
Total Product Weight (oz/yd2) 69