Ecomass® 1066ZD96 Tungsten Filled Polyamide
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Ecomass Technologies |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ecomass® 1066ZD96 Tungsten Filled Polyamide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nontoxic alternative to Lead (Pb), weighting and balancing applicationsHigh Specific GravityTungsten Powder Filled Polyamide (PA) AlloyGood ToughnessInformation provided by Technical Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 10.0 g/cc | 10.0 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0060 cm/cm | 0.0050 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 34.5 MPa | 5000 psi | ASTM D638 |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| Tensile Modulus | 6.45 GPa | 935 ksi | ASTM D638 |
| Flexural Strength | 48.3 MPa | 7000 psi | ASTM D790 |
| Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm | 2.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | 0.25 ohm | 0.25 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 254 °C | 400 - 490 °F | |
| Mold Temperature | 57.2 - 82.2 °C | 135 - 180 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 4 hour | 4 hour |
Users viewing this material also viewed the following:
- NextGen Adhesives M907-20 Medical Grade Epoxy Adhesive
- SABIC Innovative Plastics Lexan® HFD1930 PC Copolymer (Asia Pacific)
- Ineos ABS Lustran® 2710, Extrusion Grade (discontinued **)
- Albis Plastics Cellulose Acetate Propionate CP801 (UV Inhibitor Added), 13% Plasticizer (discontinued **)
- Momentive Performance Materials SS4004P Silicone Primer for use with RTV Silicone Adhesive Sealants, Pink
- Saint-Gobain CHR® 2925-7 Glass-Foil Backing Silicone Adhesive Pressure Sensitive Tape
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR N774 (SRF) Filler
- Fainplast Compounds MPH 57 Medical Flexible PVC, Extrusion
- Advanced Polymer Alloys DuraGrip™ DGR 6140 UT Thermoplastic Elastomer (TPE)
Copyright © lookpolymers.com All Rights Reserved