Eastman 9921P PET Film (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Eastman 9921P PET Film (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Voridian PET 9921P is produced at Voridian’s manufacturing sites in Rotterdam and Zarate, it is PTA/CHDM based, and it is sold to customers in the Europe, Middle East and Africa, Argentina, Bolivia, Brazil, Chile, Colombia, Mexico, Paraguay, Peru, Uruguay and Venezuela. Voridian PET 9921P will be used primarily for thick wall applications such as refill bottles for water and carbonated soft drinks.Applications/UsesAPET and thick sheetBeverage packagingCustom containersThick wall containersBottlesSealing layer for CPET traysRefillable bottles

Physical Properties	Metric	English	Comments
Bulk Density	0.803 g/cc	0.0290 lb/in³	Poured; ASTM D1895
	0.881 g/cc	0.0318 lb/in³	Vibrated; ASTM D1895
Density	1.30 g/cc	0.0470 lb/in³	Film; ASTM D1505
	1.40 g/cc	0.0506 lb/in³	Crystalline Density; ASTM D1505
Melt Density	1.20 g/cc @Temperature 285 °C	0.0434 lb/in³ @Temperature 545 °F	ASTM D1238
Viscosity Measurement	0.78	0.78	Intrinsic; EMN-A-AC-G-V-1
	0.78 - 0.82	0.78 - 0.82	Pellet, Intrinsic; VGAS-A-AN-G-V-1
Thickness	250 microns	9.84 mil

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	55.0 MPa	7980 psi	ASTM D882
Film Tensile Strength at Yield, TD	53.0 MPa	7690 psi	ASTM D882
Film Elongation at Break, MD	600 %	600 %	ASTM D882
Film Elongation at Break, TD	600 %	600 %	ASTM D882
Film Elongation at Yield, MD	6.0 %	6.0 %	ASTM D882
Film Elongation at Yield, TD	6.0 %	6.0 %	ASTM D882
Tensile Modulus	2.00 GPa	290 ksi	TD; ASTM D882
	2.10 GPa	305 ksi	MD; ASTM D882
Izod Impact, Unnotched (ISO)	NB	NB	ISO 180
	181 kJ/m² @Temperature -40.0 °C	86.1 ft-lb/in² @Temperature -40.0 °F	ISO 180
Tear Strength, Total	92.0 N	20.7 lb (f)	PPT Tear Resistance, MD; ASTM D2582
	106 N	23.8 lb (f)	PPT Tear Resistance, TD; ASTM D2582
Elmendorf Tear Strength, MD	3.14 g/micron	79.8 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	3.236 g/micron	82.19 g/mil	ASTM D1922
Dart Drop	1.08 g/micron	27.4 g/mil	at -18°C; ASTM D1709
	1.876 g/micron	47.65 g/mil	23°C; ASTM D1709
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
Film Tensile Strength at Break, TD	48.0 MPa	6960 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Heat of Fusion	61.0 J/g	26.2 BTU/lb	ASTM E793
Specific Heat Capacity	1.20 J/g-°C	0.287 BTU/lb-°F	ASTM E1269
	1.40 J/g-°C @Temperature 80.0 °C	0.335 BTU/lb-°F @Temperature 176 °F	ASTM E1269
	1.60 J/g-°C @Temperature 100 °C	0.382 BTU/lb-°F @Temperature 212 °F	ASTM E1269
	2.00 J/g-°C @Temperature 200 °C	0.478 BTU/lb-°F @Temperature 392 °F	ASTM E1269
	2.10 J/g-°C @Temperature 280 °C	0.502 BTU/lb-°F @Temperature 536 °F	ASTM E1269
Melting Point	239 °C	462 °F	Crystalline Peak Melting Point; ASTM D3418

Optical Properties	Metric	English	Comments
Haze	0.40 %	0.40 %	ASTM D1003
Gloss	111 %	111 %	at 45°; ASTM D2457
Transmission, Visible	90 %	90 %	Regular Transmittance; ASTM D1003
	92 %	92 %	Total Transmittance; ASTM D1003
	99 %	99 %	Clarity; ASTM D1003

Descriptive Properties	Value	Comments
Acetaldehyde	<1ppm	VKCA-A-AS-G-GC-0001
Color, CIE a*	-0.02	VGAS-A-AN-G-RS-001
Color, CIE b*	0.37	VGAS-A-AN-G-RS-001
Color, CIE L*	96	VGAS-A-AN-G-RS-001
Fines, wt%, max	0.05	VGAS-A-AN-G-GA-1
Pellet Shape	Rectangular 2x2x3 mm