EPICHEM Epinyl PA 6 Polyamide 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | EPICHEM srl |
| Trade Name | Epinyl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EPICHEM Epinyl PA 6 Polyamide 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: medium viscosity, good mechanical properties
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 9.0 % @Temperature 23.0 °C |
9.0 % @Temperature 73.4 °F |
24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0070 - 0.012 cm/cm | 0.0070 - 0.012 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 85 - 100 | 85 - 100 | ASTM D785, ISO 2039/2 |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638, ISO R527 |
| Elongation at Break | 65 - 100 % | 65 - 100 % | ASTM D638, ISO R527 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.500 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.937 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256, ISO 180/4a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | 20000 h; VDE 0304/P2-1, IEC 216 |
| 85.0 °C | 185 °F | 5000 h; VDE 0304/P2-1, IEC 216 | |
| 180 °C | 356 °F | few hours; VDE 0304/P2-1, IEC 216 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 192 °C @Load 5.00 kg |
378 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
| 205 °C @Load 0.999 kg |
401 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.4 @Frequency 1000 Hz |
3.4 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | VDE 0303-P1, IEC 112 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 T 40 Polyamide 66, 40% Mineral Filled
- Overview of materials for Polystyrene + Polyphenylene Ether, Glass + Mineral Filler
- Guarniflon PTFE G427 Polytetrafluoroethylene 40% Bronze, 5% Molybdenum Disulfide
- LG Chemical LUPOL GP-3154F General Purpose Polypropylene, 15% Mineral Fillers, High Modulus, Flame Retardant
- UBE UBESTA® 3030JI9L Plasticized Automotive Grade Nylon 12
- Wieland 1932 Wilaform Palladium
- Dow Tyrin® 3615P Chlorinated Polyethylene Elastomer
- Huntsman PE1059 Film Extrusion Polyethylene (discontinued **)
- Arlon 47571R012 0.012" Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved