EMS-Grivory Grivory® TSC-40/4 EC black 9832 PA666-CF40
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® TSC-40/4 EC black 9832 PA666-CF40.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Water Absorption | 5.0 % | 5.0 % | ISO 62 |
| Moisture Absorption | 1.50 % | 1.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 110 MPa | 16000 psi | conditioned; ISO 2039-1 |
| 190 MPa | 27600 psi | dry; ISO 2039-1 | |
| Tensile Strength at Break | 200 MPa | 29000 psi | conditioned; ISO 527-1/-2 |
| 260 MPa | 37700 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.0 % | 2.0 % | dry; ISO 527-1/-2 |
| 4.0 % | 4.0 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 17.0 GPa | 2470 ksi | conditioned; ISO 527-1/-2 |
| 26.0 GPa | 3770 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | dry; ISO 179/1eU |
| 8.50 J/cm² | 40.4 ft-lb/in² | conditioned; ISO 179/1eU | |
| 5.00 J/cm² @Temperature 30.0 °C |
23.8 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 5.00 J/cm² @Temperature 30.0 °C |
23.8 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | dry; ISO 179/1eA |
| 1.60 J/cm² | 7.61 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.700 J/cm² @Temperature 30.0 °C |
3.33 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 0.700 J/cm² @Temperature 30.0 °C |
3.33 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 90.0 - 120 °C | 194 - 248 °F | long term; EMS |
| 200 °C | 392 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 185 °C | 365 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | dry; IEC 60093 |
| 10000 ohm-cm | 10000 ohm-cm | conditioned; IEC 60093 | |
| Surface Resistance | 100 ohm | 100 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Automotive electr. and electronics, lighting | |
| Powertrain and Chassis | ||
| Electricals & Electronics | Electrical appliances | |
| Electrical equipment | ||
| Form | Granules | |
| Industry & Consumer goods | Mechanical Engineering | |
| Power transmission | ||
| Sports & Leisure | ||
| Tools & Accessories | ||
| Processing | Injection Molding | |
| Product Attributes | Improved friction & wear properties | |
| Special Characteristics | Anti-static |
Users viewing this material also viewed the following:
- MV Labs HG600 HgI2 Mercury(II) iodide
- PolyOne Therma-Tech™ NN-3000 TC Polyamide 66 (Nylon 66)
- Proto3000 Objet TangoBlack FullCure970 Rubber-like Prototyping Polymer
- MetalTek MTEK 230-N Cast UNS C95800 Aluminum Bronze
- SABIC Innovative Plastics ULTEM XH6050 PEI Copolymer
- SABIC Innovative Plastics NORYL PX1180 PPE+HIPS (Europe-Africa-Middle East)
- Master Bond EP37-3FLSP Optically Clear Epoxy Has Low Exotherm
- Tipco Tipcolene® FPTC 60 - 60% Talc & Calcium Carbonate Reinforced Polypropylene Homopolymer Masterbatch
- A. Schulman ComAlloy Comtuf® 525 Polycarbonate/Styrenic Alloy
Copyright © lookpolymers.com All Rights Reserved