Total Xsene® BM 593 HDPE, blow molding

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer Total Atofina
Trade Name XSene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total Xsene® BM 593 HDPE, blow molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FINATHENE® BM 593 is a new generation of bimodal high density polyethylene based on hexene (C6) as co-monomer and is produced by the ATOFINA Double Loop Technology™. FINATHENE® BM 593 has been especially designed for the manufacture of blow molded bottles for aggressive liquids (up to 5 liters). Typical applications are bottles for the packaging of liquid detergents and personal care products. FINATHENE® BM 593 has a broad (bimodal) molecular weight distribution that ensures easy processing, high machine output and bottles with a good surface finish. Due to the combination of hexene (C6) co-monomer and a bimodal molecular weight distribution, FINATHENE® BM 593 offers an excellent balance between stiffness and environmental stress crack resistance. This ensures a high security of stacking during transit and storage of bottles. FINATHENE® BM 593 is best processed at temperatures between 180 and 220°C.Information provided by Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.
Physical Properties Metric English Comments
Density 0.959 g/cc
0.0346 lb/in³
ISO 1183
Environmental Stress Crack Resistance >= 200 hour
>= 200 hour
ASTM D1693-70
Melt Flow 0.27 g/10 min

@Load 2.16 kg
0.27 g/10 min

@Load 4.76 lb
ISO 1133
High Load Melt Index 26 g/10 min

@Load 21.6 kg
26 g/10 min

@Load 47.6 lb
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 28.0 MPa
4060 psi
ISO 527
Tensile Strength, Yield 31.0 MPa
4500 psi
ISO 527
Elongation at Break >= 700 %
>= 700 %
ISO 527
Elongation at Yield 7.0 %
7.0 %
ISO 527
Flexural Modulus 1.55 GPa
225 ksi
ISO 178