EMS-Grivory Grivory® HT3Z LF black 9564 PA*

Category	Polymer , Thermoplastic , Nylon
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® HT3Z LF black 9564 PA*.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product description: Grivory HT3Z LF is an unreinforced and impact resistant, PTFE modified engineering thermoplastic based on semi crystalline partially aromatic copolyamide. This Grivory HT product is partially based on renewable raw materials. ISO polymer designation: PA 10T/X ASTM designation: PPA, polyphthalamide Grivory HT3Z LF is especially used in tribological applications. Grivory HT3Z LF exhibits low moisture absorption, high stiffness and high heat distortion temperature. The PTFE (polytetrafluoroethylene) modification reduces the sliding friction after a short initial phase. As each tribological system has its own properties (material combination, temperature, force etc.), the suitability of the product has to be tested for each application under practical conditions.Information provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in³	ISO 1183
Water Absorption	2.5 %	2.5 %	ISO 62
Moisture Absorption	1.40 %	1.40 %	ISO 62
Linear Mold Shrinkage, Flow	0.018 cm/cm	0.018 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.012 cm/cm	0.012 in/in	ISO 294-4, 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	140 MPa	20300 psi	dry; ISO 2039-1
	140 MPa	20300 psi	conditioned; ISO 2039-1
Tensile Strength at Break	75.0 MPa	10900 psi	conditioned; ISO 527-1/-2
	80.0 MPa	11600 psi	dry; ISO 527-1/-2
Elongation at Break	3.0 %	3.0 %	dry; ISO 527-1/-2
	4.0 %	4.0 %	conditioned; ISO 527-1/-2
Tensile Modulus	2.70 GPa	392 ksi	dry; ISO 527-1/-2
	2.80 GPa	406 ksi	conditioned; ISO 527-1/-2
Charpy Impact Unnotched	9.50 J/cm²	45.2 ft-lb/in²	conditioned; ISO 179/1eU
	10.0 J/cm²	47.6 ft-lb/in²	dry; ISO 179/1eU
	9.00 J/cm² @Temperature 30.0 °C	42.8 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU
	9.50 J/cm² @Temperature 30.0 °C	45.2 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	dry; ISO 179/1eA
	0.600 J/cm²	2.86 ft-lb/in²	conditioned; ISO 179/1eA
	0.600 J/cm² @Temperature 30.0 °C	2.86 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	0.600 J/cm² @Temperature 30.0 °C	2.86 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	80.0 µm/m-°C	44.4 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	80.0 µm/m-°C	44.4 µin/in-°F	ISO 11359-1/-2
Melting Point	295 °C	563 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	140 °C	284 °F	long term; EMS
	240 °C	464 °F	short term; EMS
Deflection Temperature at 1.8 MPa (264 psi)	110 °C	230 °F	ISO 75-1/-2
Deflection Temperature at 8.0 MPa	85.0 °C	185 °F	ISO 75-1/-2
Flammability, UL94	HB	HB	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	dry; IEC 60093
	1.00e+12 ohm-cm	1.00e+12 ohm-cm	conditioned; IEC 60093
Surface Resistance	1.00e+11 ohm	1.00e+11 ohm	IEC 60093
Dielectric Strength	33.0 kV/mm	838 kV/in	dry; IEC 60243-1
	33.0 kV/mm	838 kV/in	conditioned; IEC 60243-1
Comparative Tracking Index	400 V	400 V	conditioned; IEC 60112

Descriptive Properties	Value	Comments
Automotive	Air intake sytems
	Compressed air systems
	Cooling and climate control
	Fuel systems
	Hydraulic systems
	Interior
	Powertrain and Chassis
Electricals & Electronics	Electrical appliances
	Electrical equipment
Form	Granules
Industry & Consumer goods	Hydraulics & Pneumatics
	Mechanical Engineering
	Power transmission
	Tools & Accessories
Processing	Injection Molding
Product Attributes	Bio based Polyamide
	Co Polyamide
	Hydrolysis resistant
	Improved alcohol resistance
	Partially aromatic Polyamide
Special Characteristics	Improved heat resistance
	Platable