Crucible Steel Aquamet® 18 Stainless Steel

Category	Metal , Ferrous Metal , Austenitic , Stainless Steel
Manufacturer	Crucible Steel
Trade Name	Aquamet®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Crucible Steel Aquamet® 18 Stainless Steel.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AQUAMET 18 is an austenitic stainless steel with corrosion resistance comparable to that of Type 304. Its good strength and toughness make it an ideal shafting material for workboats. It provides a stainless alternative to ABS Grade 2 carbon steel shafting, but requires no sleeves nor fiberglass. In certain large diameters, it does offer a strength advantage over AQUAMET 19. (See properties below.) It is frequently used on pusher tugs, tow boats, supply boats and fishing trawlers. NOTE: AQUAMET 18 is currently available by special order on a heat lot basis only.Information provided by Crucible Specialty Metals.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	621 MPa @Thickness 203 - 305 mm	90000 psi @Thickness 8.00 - 12.0 in
	827 MPa @Thickness <=44.5 mm	120000 psi @Thickness <=1.75 in
Tensile Strength, Yield	345 MPa @Strain 0.200 %, Thickness 203 - 305 mm	50000 psi @Strain 0.200 %, Thickness 8.00 - 12.0 in	Tension
	621 MPa @Strain 0.200 %, Thickness <=44.5 mm	90000 psi @Strain 0.200 %, Thickness <=1.75 in	Tension
Elongation at Break	35 %	35 %	in 2"; 8" to 12"
	20 % @Thickness <=44.5 mm	20 % @Thickness <=1.75 in	in 2"
Reduction of Area	45 % @Thickness 203 - 305 mm	45 % @Thickness 8.00 - 12.0 in
	50 % @Thickness <=44.5 mm	50 % @Thickness <=1.75 in
Shear Strength	228 MPa @Strain 0.200 %, Thickness 203 - 305 mm	33000 psi @Strain 0.200 %, Thickness 8.00 - 12.0 in
	414 MPa @Strain 0.200 %, Thickness <=44.5 mm	60000 psi @Strain 0.200 %, Thickness <=1.75 in

Component Elements Properties	Metric	English	Comments
Carbon, C	<= 0.15 %	<= 0.15 %
Chromium, Cr	16.5 - 19 %	16.5 - 19 %
Iron, Fe	>= 62.81 %	>= 62.81 %	As Remainder
Manganese, Mn	11 - 14 %	11 - 14 %
Nickel, Ni	0.50 - 2.5 %	0.50 - 2.5 %
Nitrogen, N	0.20 - 0.45 %	0.20 - 0.45 %
Phosphorous, P	<= 0.060 %	<= 0.060 %
Silicon, Si	<= 1.0 %	<= 1.0 %
Sulfur, S	<= 0.030 %	<= 0.030 %