Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
Water Absorption | 8.0 % | 8.0 % | ISO 62 |
Moisture Absorption | 2.00 % | 2.00 % | ISO 62 |
Linear Mold Shrinkage, Flow | 0.016 cm/cm | 0.016 in/in | ISO 294-4, 2577 |
Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 294-4, 2577 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Ball Indentation Hardness | 55.0 MPa | 7980 psi | conditioned; ISO 2039-1 |
95.0 MPa | 13800 psi | dry; ISO 2039-1 | |
Tensile Strength at Break | 45.0 MPa | 6530 psi | dry; ISO 527-1/-2 |
Tensile Strength, Yield | 30.0 MPa | 4350 psi | dry; ISO 527-1/-2 |
45.0 MPa | 6530 psi | dry; ISO 527-1/-2 | |
Elongation at Break | 45 % | 45 % | dry; ISO 527-1/-2 |
45 % | 45 % | dry; ISO 527-1/-2 | |
>= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |
Elongation at Yield | 5.0 % | 5.0 % | dry; ISO 527-1/-2 |
15 % | 15 % | conditioned; ISO 527-1/-2 | |
Tensile Modulus | 0.700 GPa | 102 ksi | conditioned; ISO 527-1/-2 |
1.80 GPa | 261 ksi | dry; ISO 527-1/-2 | |
Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU |
NB | NB | conditioned; ISO 179/1eU | |
NB @Temperature 30.0 °C |
NB @Temperature 86.0 °F |
dry; ISO 179/1eU | |
NB @Temperature 30.0 °C |
NB @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
Charpy Impact, Notched | 9.00 J/cm² | 42.8 ft-lb/in² | dry; ISO 179/1eA |
NB | NB | conditioned; ISO 179/1eA | |
2.00 J/cm² @Temperature 30.0 °C |
9.52 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
2.00 J/cm² @Temperature 30.0 °C |
9.52 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 |
CTE, linear, Transverse to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
Maximum Service Temperature, Air | 90.0 - 110 °C | 194 - 230 °F | long term; EMS |
220 °C | 428 °F | short term; EMS | |
Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ISO 75-1/-2 |
Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-1/-2 |
Flammability, UL94 | HB | HB | IEC 60695-11-10 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 |
1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
Dielectric Strength | 28.0 kV/mm | 711 kV/in | conditioned; IEC 60243-1 |
29.0 kV/mm | 737 kV/in | dry; IEC 60243-1 | |
Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 |
Descriptive Properties | Value | Comments |
---|---|---|
Automotive | Powertrain and Chassis | |
Electricals & Electronics | Connectors | |
Electrical appliances | ||
Form | Granules | |
Industry & Consumer goods | Housewares | |
Mechanical Engineering | ||
Sports & Leisure | ||
Tools & Accessories | ||
Processing | Injection Molding | |
Special Characteristics | High impact or impact modified |