E-Polymers Tekaloy® G70A2 Impact Resistance, Easy Molding PC/ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | E-Polymers Co. Ltd. |
| Trade Name | TEKALOY® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | E-Polymers Tekaloy® G70A2 Impact Resistance, Easy Molding PC/ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact Resistance, Easy MoldingInformation provided by E-Polymers Co. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Flexural Yield Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 6.00 J/cm | 11.2 ft-lb/in | ASTM D256 |
| 4.50 J/cm @Temperature -30.0 °C |
8.43 ft-lb/in @Temperature -22.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 - 290 °C | 428 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PP 1362R (Z21S) Propylene Homopolymer
- Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes
- Solvay Chemicals Barium carbonate standard powder
- SABIC Innovative Plastics ULTEM CRS5311 PEI (Asia Pacific)
- SMAC SMACWRAP® ST Damping Material, 0.20 mm
- Braskem LL318 LLDPE Linear Low Density Extrusion Polyethylene
- Ashley Polymers Ashlene® PB1410 Polycarbonate, 10% Glass Reinforced
- Cheng Yu Plastic E500G20 PC/PET, 20% Glass Fiber
- Axiall 02520 Plenum Flexible PVC
Copyright © lookpolymers.com All Rights Reserved