E-Polymers TEKAMID® TB120G60W , 62% Glass Fiber Reinforced PA6, DAM
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled |
| Manufacturer | E-Polymers Co. Ltd. |
| Trade Name | TEKAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | E-Polymers TEKAMID® TB120G60W , 62% Glass Fiber Reinforced PA6, DAM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High strength, weather resistanceInformation provided by E-Polymers Co. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 250 MPa | 36300 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Yield Strength | 350 MPa | 50800 psi | ASTM D790 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 |
| Izod Impact, Notched | 2.00 J/cm | 3.75 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit Teckfip™ HC FIP-C Formed in Place Conductive Elastomer
- Lehmann & Voss LUVOCOM® 1/GF/30/TF/15 Polyamide 66, with glass fiber and PTFE, heat stabilized
- SABIC Innovative Plastics Ultem DT1810E PEI Blend (Asia Pacific)
- Teijin Panlite® GS-3430 Friction and Abrasion Resistant, Glass Fiber Reinforced Polycarbonate Resin
- A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Westlake Plastics Kynar® 2850 PVDF Copolymer
- Hexcel® HexForce™ 716 Hybrid Composite Fabric
- Loctite® 417 General Purpose Ethyl Cyanoacrylate Bonding Adhesive
- Chengdu Polyster 9502 High Performance Grade TPV
- Arkema Group Oroglas® V 044 Acrylic, Extrusion Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved