ExxonMobil LDPE LD 319.92 Low Density Polyethylene Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Exxon Chemical
Trade Name	LDPE
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LDPE LD 319.92 Low Density Polyethylene Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 319.92 resin is an 8.7% vinyl acetate copolymer film resin. Film made from LD 319.92 exhibits superior impact strength and heat sealability.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: YesApplications: Meat PackagingPrimal Meat BagsInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.930 g/cc	0.0336 lb/in³	ExxonMobil method
Vinyl Acetate Content	8.7 %	8.7 %	ExxonMobil Method
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	330 %	330 %	ASTM D882
Film Elongation at Break, TD	660 %	660 %	ASTM D882
Puncture Energy	3.62 J	2.67 ft-lb	ExxonMobil Method
Elmendorf Tear Strength MD	120 g	120 g	ASTM D1922
Elmendorf Tear Strength TD	100 g	100 g	ASTM D1922
Dart Drop Test	250 g	0.551 lb	ASTM D1709A
Film Tensile Strength at Break, MD	30.3 MPa	4400 psi	ASTM D882
Film Tensile Strength at Break, TD	27.6 MPa	4000 psi	ASTM D882
1% Secant Modulus, MD	110 MPa	16000 psi	ASTM D882
1% Secant Modulus, TD	117 MPa	17000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 210 °C	<= 410 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	1.5 %	1.5 %	ASTM D1003
Gloss	88 %	88 %	45°; ASTM D2457

Descriptive Properties	Value	Comments
Puncture Force	16 lbf	ExxonMobil Method