DuPont Performance Polymers Zytel® HTN 53G50LWSF BK702A Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN 53G50LWSF BK702A Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
50% Glass Reinforced High Performance Polyamide with Low Warpage and High Stiffness Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 210 MPa
30500 psi
50%RH; ISO 527-1/-2
270 MPa
39200 psi
DAM; ISO 527-1/-2
Elongation at Break 2.4 %
2.4 %
DAM; ISO 527-1/-2
2.6 %
2.6 %
50%RH; ISO 527-1/-2
Tensile Modulus 16.0 GPa
2320 ksi
50%RH; ISO 527-1/-2
17.0 GPa
2470 ksi
DAM; ISO 527-1/-2
Charpy Impact Unnotched 9.00 J/cm²
42.8 ft-lb/in²
50%RH; ISO 179/1eU
9.00 J/cm²
42.8 ft-lb/in²
DAM; ISO 179/1eU
9.00 J/cm²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eU
9.00 J/cm²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eU
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
DAM; ISO 179/1eA
1.60 J/cm²
7.61 ft-lb/in²
50%RH; ISO 179/1eA
1.40 J/cm²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eA
1.60 J/cm²

@Temperature -30.0 °C
 7.61 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour 11000 MPa

@Time 3600 sec
 1.60e+6 psi

@Time 1.00 hour
 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours 8000 MPa

@Time 3.60e+6 sec
 1.16e+6 psi

@Time 1000 hour
 50%RH; ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 19.0 µm/m-°C
10.6 µin/in-°F
DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 59.0 µm/m-°C
32.8 µin/in-°F
DAM; ISO 11359-1/-2
Melting Point 260 °C
500 °F
DAM; first heat; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
DAM; ISO 75-1/-2
Flammability, UL94 HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 DAM; IEC 60695-11-10
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 DAM; IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
DAM; IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
50%RH; IEC 60093
Comparative Tracking Index 550 V
550 V
DAM; IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Delivery Form Pellets
Processing Injection Moulding
Regional Availability Asia Pacific