- DuPont Performance Polymers Zytel® BM73G15THS BK317 Nylon 6 (Unverified Data**)
DuPont Performance Polymers Zytel® BM73G15THS BK317 Nylon 6 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® BM73G15THS BK317 Nylon 6
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® BM73G15THS is a 15% glass fiber reinforced, heat stabilized, lubricated, toughened polyamide 6 for blow molding.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | DAM; ISO 1183 |
| Filler Content | 15 % | 15 % | DAM |
| Linear Mold Shrinkage, Flow | 0.0028 cm/cm @Thickness 2.00 mm |
0.0028 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa @Temperature 23.0 °C |
9430 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 107 MPa @Temperature 23.0 °C |
15500 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 5.7 % @Temperature 23.0 °C |
5.7 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 22 % @Temperature 23.0 °C |
22 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 2.50 GPa @Temperature 23.0 °C |
363 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 5.10 GPa @Temperature 23.0 °C |
740 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU |
| 11.5 J/cm² @Temperature 23.0 °C |
54.7 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eU | |
| Charpy Impact, Notched | 2.70 J/cm² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| 3.30 J/cm² @Temperature 23.0 °C |
15.7 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | DAM; ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 °C | 518 °F | DAM; Optimum |
| 260 - 280 °C | 500 - 536 °F | DAM | |
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | DAM |
| 80.0 °C | 176 °F | DAM; optimum | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.030 % | <= 0.030 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Filler | Glass fiber reinforcement | DAM |
| Forms | Pellets | DAM |
| Generic | Nylon 6 | DAM |
| Material Status | Preliminary Data | DAM |
| Part Marking Code | >PA6-IGF15< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA6 | DAM |
| Processing Method | Blow Molding | DAM |
| Product Category | Blow Moldable Resins | DAM |
| Glass Reinforced Resins | DAM | |
| Toughened Resins | DAM | |
| Region Available - Global | Yes | DAM |
| Resin Identification | PA6-IGF15 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
Users viewing this material also viewed the following:
- Outokumpu 4567 Austenitic Stainless Steel
- LG Chemical LS130S PVC
- Techmer ES HiFill® PA6/6 GF33 NAT001 33% Glass Filled
- A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer
- Cytec Thornel® T-650/35 6K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
- Clariant Renol PPT10 Polypropylene Copolymer, Talc Filled
- 3M Scotch-Weld™ Foam Fast 74 Adhesive
- Amco PRIMATOP HDPE 003955BAS Hexene Copolymer
- Axiall 8450 Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved