ExxonMobil Bicor® 70 PXS OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor® 70 PXS OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor PXS is one-side sealable, PVdC-coated OPP film designed for use as the inside sealant web in laminations.Availability: Latin America, North America and South AmericaKey Features:Excellent crimp seal strength and seal rangeExcellent hot tack for VFFS applicationsExcellent flavor and aroma barrierVery good moisture and oxygen barriersLap sealable to an acrylic-coated outer webFeatures:Flavor & Aroma BarrierGas BarrierHigh Barrier PVdC CoatedIn Lamination Lap SealableMoisture BarrierOxygen BarrierPVdC CoatedSealable High Barrier PVdC CoatedApplications:Biscuits/Cookie/CrackersConfectionery, GumConfectionery, SugarCrisps and SnacksUses:HFF Flexible PackagingPre-made Bags - Flexible PackagingVFFS Flexible PackagingProcessing Method: Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Solvent Flexographic Printing and Solvent Rotogravure Printing Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 4.20 g/m²/day | 0.270 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Oxygen Transmission Rate | 15.0 cc/m²/day | 0.966 cc/100 in²/day | 23°C, 0% RH; ExxonMobil Method |
| Thickness | 17.8 microns | 0.700 mil | Nominal; ExxonMobil Method |
| Coating Weight | 16.8 g/m² | 10.5 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Break, MD | 121 MPa | 17500 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 221 MPa | 32000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 3.5 % | 3.5 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 2.0 % | 2.0 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.0 % | 1.0 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crimp Seal MST | 210°F | PVdC/PVdC, 200g/in |
| Crimp Seal Strength | 520 g/in | PVdC/PVdC, 260°F, 20psi, 3/4sec |
| Yield | 41000 in2/lb |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA-927 Impact Modified Acrylic Resin
- Quadrant EPP TIVAR® ESD Electro Static Dissipative UHMW-PE (ASTM Product Data Sheet)
- SABIC Innovative Plastics LNP LUBRICOMP OCP36A PPS - Branched (Asia Pacific)
- UBE UBEPOL BR153A Oil-Extended BR Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- Master Bond SteelMaster 43HT Stainless Steel Filled Two Component Epoxy System
- A. Schulman POLYBATCH™ Blue LL40348/4 Concentrate Based In LLDPE
- CP-Polymer-Technik Wellamid® 6000 HWCP Nylon 6, Heat Stabilized, Conditioned
- Braskem LH537 LLDPE Cast Film Extrusion Polyethylene
Copyright © lookpolymers.com All Rights Reserved