DuPont Performance Polymers Rynite® 935SUV BK593 Polyethylene Terephthalate (PET)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 40% Glass Reinforced
Manufacturer DuPont Performance Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® 935SUV BK593 Polyethylene Terephthalate (PET)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
35% Glass Reinforced UV Stabilized Polyethylene Terephthalate Rynite 935SUV BK593 is a 35% glass fiber /mineral reinforced UV stabilized modified polyethylene terephthalate resin with low warpage developed for long-term outdoor applications.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.57 g/cc
0.0567 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
ISO 527-1/-2
Tensile Stress 1.94 MPa

@Strain 0.0700 %,
Temperature 150 °C
 281 psi

@Strain 0.0700 %,
Temperature 302 °F
 ISO 11403-1 -2
2.36 MPa

@Strain 0.0400 %,
Temperature 90.0 °C
 342 psi

@Strain 0.0400 %,
Temperature 194 °F
 ISO 11403-1 -2
2.79 MPa

@Strain 0.0300 %,
Temperature 0.000 °C
 405 psi

@Strain 0.0300 %,
Temperature 32.0 °F
 ISO 11403-1 -2
3.57 MPa

@Strain 0.0300 %,
Temperature -20.0 °C
 518 psi

@Strain 0.0300 %,
Temperature -4.00 °F
 ISO 11403-1 -2
3.84 MPa

@Strain 0.0300 %,
Temperature 40.0 °C
 557 psi

@Strain 0.0300 %,
Temperature 104 °F
 ISO 11403-1 -2
3.89 MPa

@Strain 0.0400 %,
Temperature -40.0 °C
 564 psi

@Strain 0.0400 %,
Temperature -40.0 °F
 ISO 11403-1 -2
4.27 MPa

@Strain 0.0300 %,
Temperature 23.0 °C
 619 psi

@Strain 0.0300 %,
Temperature 73.4 °F
 ISO 11403-1 -2
6.42 MPa

@Strain 0.290 %,
Temperature 150 °C
 931 psi

@Strain 0.290 %,
Temperature 302 °F
 ISO 11403-1 -2
6.93 MPa

@Strain 0.170 %,
Temperature 90.0 °C
 1010 psi

@Strain 0.170 %,
Temperature 194 °F
 ISO 11403-1 -2
8.95 MPa

@Strain 0.110 %,
Temperature 0.000 °C
 1300 psi

@Strain 0.110 %,
Temperature 32.0 °F
 ISO 11403-1 -2
10.36 MPa

@Strain 0.110 %,
Temperature -20.0 °C
 1503 psi

@Strain 0.110 %,
Temperature -4.00 °F
 ISO 11403-1 -2
10.74 MPa

@Strain 0.100 %,
Temperature 40.0 °C
 1558 psi

@Strain 0.100 %,
Temperature 104 °F
 ISO 11403-1 -2
11.09 MPa

@Strain 0.110 %,
Temperature -40.0 °C
 1608 psi

@Strain 0.110 %,
Temperature -40.0 °F
 ISO 11403-1 -2
11.87 MPa

@Strain 0.110 %,
Temperature 23.0 °C
 1722 psi

@Strain 0.110 %,
Temperature 73.4 °F
 ISO 11403-1 -2
22.09 MPa

@Strain 2.48 %,
Temperature 150 °C
 3204 psi

@Strain 2.48 %,
Temperature 302 °F
 ISO 11403-1 -2
23.21 MPa

@Strain 0.250 %,
Temperature 40.0 °C
 3366 psi

@Strain 0.250 %,
Temperature 104 °F
 ISO 11403-1 -2
24.94 MPa

@Strain 4.68 %,
Temperature 150 °C
 3617 psi

@Strain 4.68 %,
Temperature 302 °F
 ISO 11403-1 -2
25.99 MPa

@Strain 0.250 %,
Temperature 23.0 °C
 3770 psi

@Strain 0.250 %,
Temperature 73.4 °F
 ISO 11403-1 -2
26.74 MPa

@Strain 8.76 %,
Temperature 150 °C
 3878 psi

@Strain 8.76 %,
Temperature 302 °F
 ISO 11403-1 -2
30.0 MPa

@Strain 1.15 %,
Temperature 90.0 °C
 4350 psi

@Strain 1.15 %,
Temperature 194 °F
 ISO 11403-1 -2
30.74 MPa

@Strain 0.310 %,
Temperature 0.000 °C
 4458 psi

@Strain 0.310 %,
Temperature 32.0 °F
 ISO 11403-1 -2
32.66 MPa

@Strain 0.300 %,
Temperature -20.0 °C
 4737 psi

@Strain 0.300 %,
Temperature -4.00 °F
 ISO 11403-1 -2
35.35 MPa

@Strain 0.310 %,
Temperature -40.0 °C
 5127 psi

@Strain 0.310 %,
Temperature -40.0 °F
 ISO 11403-1 -2
38.74 MPa

@Strain 2.48 %,
Temperature 90.0 °C
 5619 psi

@Strain 2.48 %,
Temperature 194 °F
 ISO 11403-1 -2
40.33 MPa

@Strain 5.44 %,
Temperature 90.0 °C
 5849 psi

@Strain 5.44 %,
Temperature 194 °F
 ISO 11403-1 -2
52.44 MPa

@Strain 0.770 %,
Temperature 40.0 °C
 7606 psi

@Strain 0.770 %,
Temperature 104 °F
 ISO 11403-1 -2
62.03 MPa

@Strain 0.820 %,
Temperature 23.0 °C
 8997 psi

@Strain 0.820 %,
Temperature 73.4 °F
 ISO 11403-1 -2
70.05 MPa

@Strain 0.870 %,
Temperature 0.000 °C
 10160 psi

@Strain 0.870 %,
Temperature 32.0 °F
 ISO 11403-1 -2
71.79 MPa

@Strain 2.36 %,
Temperature 40.0 °C
 10410 psi

@Strain 2.36 %,
Temperature 104 °F
 ISO 11403-1 -2
76.17 MPa

@Strain 0.800 %,
Temperature -20.0 °C
 11050 psi

@Strain 0.800 %,
Temperature -4.00 °F
 ISO 11403-1 -2
78.37 MPa

@Strain 0.720 %,
Temperature -40.0 °C
 11370 psi

@Strain 0.720 %,
Temperature -40.0 °F
 ISO 11403-1 -2
84.17 MPa

@Strain 2.30 %,
Temperature 23.0 °C
 12210 psi

@Strain 2.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
100.7 MPa

@Strain 2.25 %,
Temperature 0.000 °C
 14610 psi

@Strain 2.25 %,
Temperature 32.0 °F
 ISO 11403-1 -2
117.13 MPa

@Strain 2.01 %,
Temperature -20.0 °C
 16988 psi

@Strain 2.01 %,
Temperature -4.00 °F
 ISO 11403-1 -2
130.53 MPa

@Strain 1.71 %,
Temperature -40.0 °C
 18932 psi

@Strain 1.71 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Elongation at Break 2.3 %
2.3 %
ISO 527-1/-2
Tensile Modulus 9.70 GPa
1410 ksi
ISO 527-1/-2
Secant Modulus 4.21 GPa

@Strain 1.66 %,
Temperature 40.0 °C
 611 ksi

@Strain 1.66 %,
Temperature 104 °F
 ISO 11403-1 -2
4.8491 GPa

@Strain 1.67 %,
Temperature 23.0 °C
 703.31 ksi

@Strain 1.67 %,
Temperature 73.4 °F
 ISO 11403-1 -2
5.59 GPa

@Strain 1.68 %,
Temperature 0.000 °C
 811 ksi

@Strain 1.68 %,
Temperature 32.0 °F
 ISO 11403-1 -2
5.92 GPa

@Strain 1.01 %,
Temperature 40.0 °C
 858 ksi

@Strain 1.01 %,
Temperature 104 °F
 ISO 11403-1 -2
6.58 GPa

@Strain 1.06 %,
Temperature 23.0 °C
 954 ksi

@Strain 1.06 %,
Temperature 73.4 °F
 ISO 11403-1 -2
6.99 GPa

@Strain 1.53 %,
Temperature -20.0 °C
 1010 ksi

@Strain 1.53 %,
Temperature -4.00 °F
 ISO 11403-1 -2
7.16 GPa

@Strain 1.11 %,
Temperature 0.000 °C
 1040 ksi

@Strain 1.11 %,
Temperature 32.0 °F
 ISO 11403-1 -2
8.14 GPa

@Strain 0.110 %,
Temperature 0.000 °C
 1180 ksi

@Strain 0.110 %,
Temperature 32.0 °F
 ISO 11403-1 -2
8.18 GPa

@Strain 0.470 %,
Temperature 40.0 °C
 1190 ksi

@Strain 0.470 %,
Temperature 104 °F
 ISO 11403-1 -2
8.68 GPa

@Strain 1.01 %,
Temperature -20.0 °C
 1260 ksi

@Strain 1.01 %,
Temperature -4.00 °F
 ISO 11403-1 -2
8.93 GPa

@Strain 1.30 %,
Temperature -40.0 °C
 1300 ksi

@Strain 1.30 %,
Temperature -40.0 °F
 ISO 11403-1 -2
9.30 GPa

@Strain 0.0300 %,
Temperature 0.000 °C
 1350 ksi

@Strain 0.0300 %,
Temperature 32.0 °F
 ISO 11403-1 -2
9.36 GPa

@Strain 0.550 %,
Temperature 0.000 °C
 1360 ksi

@Strain 0.550 %,
Temperature 32.0 °F
 ISO 11403-1 -2
9.40 GPa

@Strain 0.480 %,
Temperature 23.0 °C
 1360 ksi

@Strain 0.480 %,
Temperature 73.4 °F
 ISO 11403-1 -2
9.42 GPa

@Strain 0.110 %,
Temperature -20.0 °C
 1370 ksi

@Strain 0.110 %,
Temperature -4.00 °F
 ISO 11403-1 -2
9.725 GPa

@Strain 0.0400 %,
Temperature -40.0 °C
 1411 ksi

@Strain 0.0400 %,
Temperature -40.0 °F
 ISO 11403-1 -2
10.1 GPa

@Strain 0.110 %,
Temperature -40.0 °C
 1460 ksi

@Strain 0.110 %,
Temperature -40.0 °F
 ISO 11403-1 -2
10.4 GPa

@Strain 0.880 %,
Temperature -40.0 °C
 1510 ksi

@Strain 0.880 %,
Temperature -40.0 °F
 ISO 11403-1 -2
10.5 GPa

@Strain 0.530 %,
Temperature -20.0 °C
 1520 ksi

@Strain 0.530 %,
Temperature -4.00 °F
 ISO 11403-1 -2
10.74 GPa

@Strain 0.100 %,
Temperature 40.0 °C
 1558 ksi

@Strain 0.100 %,
Temperature 104 °F
 ISO 11403-1 -2
10.8 GPa

@Strain 0.110 %,
Temperature 23.0 °C
 1570 ksi

@Strain 0.110 %,
Temperature 73.4 °F
 ISO 11403-1 -2
11.5 GPa

@Strain 0.490 %,
Temperature -40.0 °C
 1670 ksi

@Strain 0.490 %,
Temperature -40.0 °F
 ISO 11403-1 -2
11.9 GPa

@Strain 0.0300 %,
Temperature -20.0 °C
 1730 ksi

@Strain 0.0300 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Users viewing this material also viewed the following: