DuPont Performance Polymers Delrin® 900P BK602 Acetal Homopolymer (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® 900P BK602 Acetal Homopolymer (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Delrin® 900P BK602 is a low viscosity black acetal homopolymer resin for multicavity and thin wall molding. It offers an improved processing thermal stability.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.42 g/cc	0.0513 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.018 cm/cm @Thickness 2.00 mm	0.018 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.017 cm/cm @Thickness 2.00 mm	0.017 in/in @Thickness 0.0787 in	ISO 294-4
Melt Flow	25 g/10 min @Load 2.16 kg, Temperature 190 °C	25 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	70.0 MPa @Temperature 23.0 °C	10200 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	17 % @Temperature 23.0 °C	17 % @Temperature 73.4 °F	nominal; ISO 527
	22 % @Temperature 23.0 °C	22 % @Temperature 73.4 °F	ISO 527
Elongation at Yield	12 % @Temperature 23.0 °C	12 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	3.30 GPa @Temperature 23.0 °C	479 ksi @Temperature 73.4 °F	ISO 527
Flexural Modulus	3.00 GPa @Temperature 23.0 °C	435 ksi @Temperature 73.4 °F	ISO 178
Izod Impact, Notched (ISO)	7.00 kJ/m² @Temperature -40.0 °C	3.33 ft-lb/in² @Temperature -40.0 °F	ISO 180/1A
	7.00 kJ/m² @Temperature 23.0 °C	3.33 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	13.0 J/cm² @Temperature 23.0 °C	61.9 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.600 J/cm² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.700 J/cm² @Temperature 23.0 °C	3.33 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA
	0.800 J/cm² @Temperature -40.0 °C	3.81 ft-lb/in² @Temperature -40.0 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	500 µm/m-°C @Temperature -40.0 - 23.0 °C	278 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	500 µm/m-°C @Temperature 23.0 - 55.0 °C	278 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	500 µm/m-°C @Temperature 55.0 - 100 °C	278 µin/in-°F @Temperature 131 - 212 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	90.0 µm/m-°C @Temperature -40.0 - 23.0 °C	50.0 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	100 µm/m-°C @Temperature 23.0 - 55.0 °C	55.6 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	130 µm/m-°C @Temperature 55.0 - 100 °C	72.2 µin/in-°F @Temperature 131 - 212 °F	ISO 11359-1/-2
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	161 °C	322 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	98.0 °C	208 °F	ISO 75-1/-2
UL RTI, Electrical	50.0 °C @Thickness 0.750 mm	122 °F @Thickness 0.0295 in	UL 746B
	110 °C @Thickness 1.50 mm	230 °F @Thickness 0.0591 in	UL 746B
	110 °C @Thickness 3.00 mm	230 °F @Thickness 0.118 in	UL 746B
UL RTI, Mechanical with Impact	50.0 °C @Thickness 0.750 mm	122 °F @Thickness 0.0295 in	UL 746B
	85.0 °C @Thickness 1.50 mm	185 °F @Thickness 0.0591 in	UL 746B
	90.0 °C @Thickness 3.00 mm	194 °F @Thickness 0.118 in	UL 746B
UL RTI, Mechanical without Impact	50.0 °C @Thickness 0.750 mm	122 °F @Thickness 0.0295 in	UL 746B
	90.0 °C @Thickness 1.50 mm	194 °F @Thickness 0.0591 in	UL 746B
	95.0 °C @Thickness 3.00 mm	203 °F @Thickness 0.118 in	UL 746B
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in	IEC 60695-11-10
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	IEC 60695-11-10
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	IEC 60695-11-10
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	UL94
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	UL94
	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in	UL94

Processing Properties	Metric	English	Comments
Melt Temperature	215 °C	419 °F	Optimum; Injection Molding
	210 - 220 °C	410 - 428 °F	Injection Molding
Mold Temperature	90.0 °C	194 °F	optimum; Injection Molding
	80.0 - 100 °C	176 - 212 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F	Injection Molding
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	Injection Molding
Moisture Content	<= 0.20 %	<= 0.20 %	Injection Molding

Descriptive Properties	Value	Comments
Appearance	Black Color
Drying Recommended	Not normally required unless moisture content of resin exceeds recommended level
Features	Creep Resistance, Good
	Dimensional Stability, Good
	Fatigue Resistant
	Homopolymer
	Stiffness, High
	Strength, High
	Viscosity, Low
Forms	Pellets
Generic	Acetal (POM) Homopolymer
Material Status	Current
Part Marking Code	>POM<	ISO 11469
Polymer Family	POM
Polymer Type	POM Homopolymer
Processing Method	Injection Molding
Product Category	Unreinforced Resins
Region Available - Global	Yes
Resin Identification	POM	ISO 1043
RoHS Compliance	Contact Manufacturer
Ultrasonic Weldable	Yes
Uses	Gears
	General Purpose
	Parts, Engineering
	Parts, Thin-walled