SABIC Innovative Plastics PC6300 PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics PC6300 PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC6300 resin is a very high flow (MFR = 9.5 at 250ºC/1.2kg) polycarbonate product designed for use in the optical media market.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.35 %

@Temperature 23.0 °C
 0.35 %

@Temperature 73.4 °F
 ASTM D 570
Water Absorption at Saturation 0.35 %

@Temperature 23.0 °C
 0.35 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on tensile bar; SABIC Method
Melt Flow 9.0 g/10 min

@Load 1.20 kg,
Temperature 250 °C
 9.0 g/10 min

@Load 2.65 lb,
Temperature 482 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
9.5 g/10 min

@Load 1.20 kg,
Temperature 250 °C
 9.5 g/10 min

@Load 2.65 lb,
Temperature 482 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D 638
60.0 MPa
8700 psi
50 mm/min; ISO 527
Elongation at Break >= 40 %
>= 40 %
Type I, 50 mm/min; ASTM D 638
>= 40 %
>= 40 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D 638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.35 GPa
341 ksi
50 mm/min; ASTM D 638
2.35 GPa
341 ksi
1 mm/min; ISO 527
Flexural Yield Strength 90.0 MPa
13100 psi
1.3 mm/min, 50 mm span; ASTM D 790
90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus 2.30 GPa
334 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.30 GPa
334 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature -30.0 °C
 5.71 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
15.0 kJ/m²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 80*10*3; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 38.9 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM C 177
0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 132 °C
270 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
132 °C

@Thickness 3.20 mm
 270 °F

@Thickness 0.126 in
 ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 122 °C
252 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
122 °C

@Thickness 3.20 mm
 252 °F

@Thickness 0.126 in
 ASTM D 648
Vicat Softening Point 138 °C
280 °F
Rate B/50; ASTM D 1525
138 °C
280 °F
Rate B/50; ISO 306
Optical Properties Metric English Comments
Refractive Index 1.586
1.586
ASTM D 542
1.586
1.586
ISO 489
Haze <= 0.70 %

@Thickness 2.54 mm
 <= 0.70 %

@Thickness 0.100 in
 ASTM D 1003
Transmission, Visible >= 90 %

@Thickness 2.54 mm
 >= 90 %

@Thickness 0.100 in
 ASTM D 1003
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
 3.0

@Frequency 1.00e+6 Hz
 IEC 60250
Dissipation Factor 0.010

@Frequency 1.00e+6 Hz
 0.010

@Frequency 1.00e+6 Hz
 IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2