DuPont Performance Polymers Crastin® S600LF NC010 PBT

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer	DuPont Performance Polymers
Trade Name	Crastin®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Crastin® S600LF NC010 PBT.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Crastin® S600LF NC010 is an unreinforced, Teflon® PTFE powder lubricated polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.32 g/cc	0.0477 lb/in³	ISO 1183
Water Absorption	0.20 % @Temperature 23.0 °C	0.20 % @Temperature 73.4 °F	Equilibrium 50%RH; ISO 62, Similar to
	0.40 % @Temperature 23.0 °C	0.40 % @Temperature 73.4 °F	Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow	0.022 cm/cm @Thickness 2.00 mm	0.022 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.022 cm/cm @Thickness 2.00 mm	0.022 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	58.0 MPa @Temperature 23.0 °C	8410 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	15 % @Temperature 23.0 °C	15 % @Temperature 73.4 °F	nominal; ISO 527
	25 % @Temperature 23.0 °C	25 % @Temperature 73.4 °F	50mm/min; ISO 527
Elongation at Yield	7.5 % @Temperature 23.0 °C	7.5 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	2.70 GPa @Temperature 23.0 °C	392 ksi @Temperature 73.4 °F	ISO 527
Flexural Strength	80.0 MPa @Temperature 23.0 °C	11600 psi @Temperature 73.4 °F	ISO 178
Izod Impact, Notched (ISO)	4.00 kJ/m² @Temperature 23.0 °C	1.90 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	10.0 J/cm² @Temperature -30.0 °C	47.6 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	14.5 J/cm² @Temperature 23.0 °C	69.0 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.300 J/cm² @Temperature -30.0 °C	1.43 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.400 J/cm² @Temperature 23.0 °C	1.90 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	225 °C	437 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	150 °C	302 °F	ISO 75-1/-2
	185 °C	365 °F	Annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C	131 °F	ISO 75-1/-2
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in	IEC 60695-11-10

Processing Properties	Metric	English	Comments
Melt Temperature	250 °C	482 °F	Optimum
	240 - 260 °C	464 - 500 °F
Mold Temperature	80.0 °C	176 °F	optimum
	30.0 - 130 °C	86.0 - 266 °F
Drying Temperature	110 - 130 °C	230 - 266 °F
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour
Moisture Content	<= 0.040 %	<= 0.040 %

Descriptive Properties	Value	Comments
Additive	Lubricant
	Lubricant, PTFE
Appearance	Natural Color
Drying Recommended	Yes
Features	Chemical Resistance, Good
	Dimensional Stability, Good
	Friction, Low
	Moisture Absorption, Low
	Processability, Good
	Wear Resistance, Good
Generic	PBT
Material Status	Current
Part Marking Code	>PBT<	ISO 11469
Polymer Family	Polyester
Polymer Type	PBT
Processing Method	Injection Molding
Product Category	Low Wear and Friction Resins
	Unreinforced Resins
Resin Identification	PBT	ISO 1043
RoHS Compliance	Contact Manufacturer
Ultrasonic Weldable	Yes
Uses	Parts, Machine/Mechanical