SABIC Innovative Plastics NORYL PPX PPX7115 PPE+PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl PPX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PPX PPX7115 PPE+PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High modulus/impact/heat PPE+PP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ISO 1183 |
| Melt Index of Compound | 12 g/10 min @Load 5.00 kg, Temperature 260 °C |
12 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 60 | 60 | ISO 2039-2 |
| Tensile Strength at Break | 31.0 MPa | 4500 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 135 % | 135 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 1.65 GPa | 239 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 51.0 MPa | 7400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.52 GPa | 220 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 36.0 kJ/m² | 17.1 ft-lb/in² | 80*10*4; ISO 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 3.70 J/cm² | 17.6 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 80.0 °C | 176 °F | Rate B/50; ISO 306 |
| 85.0 °C | 185 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Packaging 2188NT Polyvinyl Chloride, Rigid (PVC, Rigid)
- PlastiComp Complet® LCF40 - PP Homopolymer Polypropylene, 40% Long Carbon Fiber Reinforced
- Lehmann & Voss LUVOCOM® 50/CF/10/GF/10/TF/10/BK Polycarbonate, with carbon fiber, glass fiber and PTFE
- Lubrizol Advanced Materials Pearlstick® 45-60/03 Polycaprolactone based TPU
- Schwartz Technical Plastics LAMIGAMID® 1200 Cast Polyamide 12, Dry
- Master Bond UV22 One Component, UV Curable, Nanosilica Reinforced Epoxy System
- Chevron Phillips MarFlex® 5561 LDPE High Clarity, Medium Impact Film Resin
- Covestro Bayblend® FR 3030 Polycarbonate + ABS, Flame Retardant Grade
- Arlon R36338R015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- ACC MM903 Condensation Cure 2-Part Molding Rubber
Copyright © lookpolymers.com All Rights Reserved