Sibur O-55 Compound 1182 Polyvinyl Chloride (PVC)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Molded |
| Manufacturer | Sibur |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sibur O-55 Compound 1182 Polyvinyl Chloride (PVC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a period of 20 minutes. Used as a protective sheath for wires and cables operating in interval of temperatures for -55°C to 70°C. Peculiarity of plastic is its good frost resistance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 - 1.25 g/cc | 0.0426 - 0.0452 lb/in³ | |
| Water Absorption | <= 0.30 % | <= 0.30 % | |
| Collected Volatile Condensable Material | <= 2.0 % | <= 2.0 % | Loss in mass at 160°C during 6 hours |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 11.7 MPa | >= 1700 psi | |
| Elongation at Break | >= 350 % | >= 350 % |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Softening Point | 160 - 180 °C | 320 - 356 °F | |
| Brittleness Temperature | <= -55.0 °C | <= -67.0 °F | |
| Flammability Test | <= 15 | <= 15 | In seconds, method A |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+11 ohm-cm @Temperature 20.0 °C |
>= 1.00e+11 ohm-cm @Temperature 68.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Non-colored, black, white | |
| Elongation Retained After Ageing | 80% | Aged for 7 days at 100±2°C |
| Number of Inclusions | <24 psc | With dimensions up to 0.5 mm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® NX07331 PC+ABS (Asia Pacific)
- Lehmann & Voss LUVOCOM® 6-7834 Polyamide 12, lubricant modified
- Iran Petrochemical (PCC) LT0470/KJ Low Density Polyethylene
- Solvay Chemicals 1,1-Dichloro-2,2,2-trifluoroethane
- Shakespeare FL-8 Fluorocarbon PVDF Fishing Line, 15 lb
- Teknor Apex Sinvicomp SFE 5000 Polyvinyl Chloride, Flexible
- Chase Plastics CP Pryme® N100HSL (DAM) Nylon 6, Heat Stabilized, Internally Lubricated
- Polyplastics Duranex® C5315 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 15% GF filled
- Cossa Polimeri ESTACARB 0820 GF Polycarbonate, 10% Glass Filled
- Arkema Group Pebax® Rnew 40R53 SP 01 Polyether Block Amide (PEBA)
Copyright © lookpolymers.com All Rights Reserved