Plenco 7591 Phenolic, Briquette, Injection Molded
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Mineral/Flock Filled |
| Manufacturer | Plenco (Plastics Engineering Company) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plenco 7591 Phenolic, Briquette, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PLENCO 07591 is a mineral and flock cotton filled novolac phenolic molding compound. UL recognized under component file E40654.Information supplied by Plenco.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.560 g/cc | 0.0202 lb/in³ | ASTM D1895 |
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Water Absorption | 0.29 % | 0.29 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0072 cm/cm | 0.0072 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 82 | 82 | ASTM D785 |
| Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
| Elongation at Break | 0.86 % | 0.86 % | ASTM D638 |
| Tensile Modulus | 8.50 GPa | 1230 ksi | ASTM D638 |
| Flexural Strength | 79.0 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | ASTM D790 |
| Compressive Strength | 196 MPa | 28400 psi | ASTM D695 |
| Izod Impact, Notched | 0.257 J/cm | 0.481 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.256 J/cm² | 1.22 ft-lb/in² | ASTM D256 |
| Impact | 193 | 193 | J/m Drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.420 W/m-K @Temperature 100 °C |
2.91 BTU-in/hr-ft²-°F @Temperature 212 °F |
ASTM E1461 |
| Maximum Service Temperature, Air | 197 °C | 387 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 178 °C | 352 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 4.30 mm |
V-0 @Thickness 0.169 in |
|
| Shrinkage | 0.34 % | 0.34 % | 72 hr, 120ºC; ASTM D1299 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.50e+11 ohm-cm | 1.50e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.3 | 5.3 | ASTM D150 |
| Dielectric Strength | 10.2 kV/mm | 259 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.065 | 0.065 | ASTM D150 |
| Arc Resistance | 155 sec | 155 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit® 239 Primer
- Plenco 4224 Phenolic, Granular, Transfer Molded (discontinued **)
- Teknor Apex APEX® 3090-H Polyvinyl Chloride, Flexible
- Tra-Con Tra-Bond 526H02
- Hexcel® Redux® 330M Epoxy film adhesives for the bonding and finishing of composites
- Eagle Brass 316L Austenitic Stainless Steel, Annealed
- Fainplast Compounds EVAtech 807I Ethylene Vinyl Acetate Foam
- DuPont Teijin Films Mylar® EL21 Polyester Film, 1400 Gauge
- Ensinger ENSIKEM® PVDF (Polyvinylidene Fluoride) - Extruded Products (discontinued **)
- Breplast Bretene TS COR HF Dark High Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved