Dow Primacor® 1420 Ethylene Acrylic Acid (EAA)
| Category | Polymer , Film , Thermoplastic , Ethylene Acrylic Acid |
| Manufacturer | Dow Chemical |
| Trade Name | Primacor® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Primacor® 1420 Ethylene Acrylic Acid (EAA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film properties below based on a film thickness of 60 µm. Data provided by Dow Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in³ | |
| Thickness | 60.0 microns | 2.36 mil | |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg |
3.0 g/10 min @Load 4.76 lb |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 24.7 MPa | 3580 psi | Molded property |
| Film Tensile Strength at Yield, MD | 8.60 MPa | 1250 psi | |
| Film Tensile Strength at Yield, TD | 8.30 MPa | 1200 psi | |
| Tensile Strength, Yield | 9.50 MPa | 1380 psi | Molded property |
| Film Elongation at Break, MD | 515 % | 515 % | |
| Film Elongation at Break, TD | 545 % | 545 % | |
| Elongation at Break | 510 % | 510 % | Molded value |
| Tensile Modulus | 0.124 GPa | 18.0 ksi | |
| Elmendorf Tear Strength MD | 380 g | 380 g | |
| Elmendorf Tear Strength TD | 500 g | 500 g | |
| Elmendorf Tear Strength, MD | 6.30 g/micron | 160 g/mil | |
| Elmendorf Tear Strength, TD | 8.30 g/micron | 211 g/mil | |
| Dart Drop | 7.10 g/micron | 180 g/mil | |
| Film Tensile Strength at Break, MD | 37.9 MPa | 5500 psi | |
| Film Tensile Strength at Break, TD | 39.3 MPa | 5700 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 78.0 °C | 172 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % | 4.0 % | |
| Gloss | 65 % | 65 % | 45° |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 191 °C | 376 °F | Film extrusion temperature |
Users viewing this material also viewed the following:
- Momentive Performance Materials RTV6445 White Adhesive Sealant, Non-Corrosive High Strength Paste
- Lushan PA+30% GF+5% AR-1A Nylon Toughener/PA Impact Modifier
- Silberline Dedusted Flake Series DF-2750 Aluminum Flake
- ExxonMobil Diol 13 RD 40
- Trelleborg Emerson & Cuming Eccobond® G 909 One-Component Fast Cure Epoxy Adhesive
- ChevronTexaco Prediluted 50/50 Anti-Freeze/Coolant Extended Life
- ExxonMobil Label-Lyte™ 38LW280 OPP Film
- Ascend Performance Materials Vydyne® R535H NT651 Nylon 66, 35% Glass Reinforced, DAM
- ATI Allvac® 6-4ELI Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal
Copyright © lookpolymers.com All Rights Reserved