BNZ Materials BNZP-26A Insulating Firebrick (French Grade)

Category	Ceramic , Oxide , Aluminum Oxide
Manufacturer	BNZ Materials, Inc.
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BNZ Materials BNZP-26A Insulating Firebrick (French Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BNZ produces many types of Insulating Fire Brick (IFB) for use in applications from 2,000°F (1,093°C) to 3,200°F (1,760°C). Each type is formulated to meet specific thermal and physical requirements and after firing is machined to precise tolerances. Made from high purity refractory clays and other ceramic raw materials, these IFB contain a carefully graded organic filler which is burned out during manufacture to give a uniform controlled pore structure.Information provided by BNZ Materials Inc.

Physical Properties	Metric	English	Comments
Density	0.830 g/cc	0.0300 lb/in³	ASTM C134

Mechanical Properties	Metric	English	Comments
Compressive Strength	5.00 MPa	725 psi	Cold Crush Strength; ASTM C133

Thermal Properties	Metric	English	Comments
CTE, linear	7.50 µm/m-°C @Temperature 20.0 - 1000 °C	4.17 µin/in-°F @Temperature 68.0 - 1830 °F
Thermal Conductivity	0.200 W/m-K @Temperature 400 °C	1.39 BTU-in/hr-ft²-°F @Temperature 752 °F	ASTM C182
	0.218 W/m-K @Temperature 200 °C	1.51 BTU-in/hr-ft²-°F @Temperature 392 °F	ASTM C182
	0.230 W/m-K @Temperature 600 °C	1.60 BTU-in/hr-ft²-°F @Temperature 1110 °F	ASTM C182
	0.260 W/m-K @Temperature 800 °C	1.80 BTU-in/hr-ft²-°F @Temperature 1470 °F	ASTM C182
	0.290 W/m-K @Temperature 1000 °C	2.01 BTU-in/hr-ft²-°F @Temperature 1830 °F	ASTM C182
Maximum Service Temperature, Air	1400 °C	2550 °F
Shrinkage	0.50 % @Temperature 1400 °C, Time 43200 sec	0.50 % @Temperature 2550 °F, Time 12.0 hour	Permanent Linear Change; ASTM C210

Descriptive Properties	Value	Comments
Composition (%)	0.4	CaO + MgO
	2.3	Fe<sub>2</sub>O<sub>3</sub> + TiO<sub>2</sub>
	3.7	Na<sub>2</sub>O + K<sub>2</sub>O
	90.3	Al<sub>2</sub>O<sub>3</sub> + SiO<sub>2</sub>

Users viewing this material also viewed the following: