Dow AIM® 4810 High Impact Styrenic Resin

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer Dow Chemical
Trade Name AIM®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow AIM® 4810 High Impact Styrenic Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AIM® 4810 advanced styrenic resin is designed to offer the processability of high impact polystyrene and the gloss and practical toughness of high gloss ABS. It can be processed at lower temperatures than ABS, which may allow faster cycle times, energy savings or an opportunity to fill more complex molds. When used unmodified for the manufacture of food contact articles AIM 4810 complies with the US Food, Drug and Cosmetic Act and Food Additive Regulations 21 CFR 177.1640. The statute and regulations should be consulted for complete details.Data provided by Dow Chemical.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM Data
Melt Density 0.963 g/cc
0.0348 lb/in³
Melt density
Linear Mold Shrinkage 0.0055 cm/cm
0.0055 in/in
Melt Flow 8.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
8.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM Data
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 19.3 MPa
2800 psi
ASTM Data
Tensile Strength, Yield 24.5 MPa
3550 psi
ASTM Data
Elongation at Break 50 %
50 %
ASTM Data
Tensile Modulus 1.79 GPa
260 ksi
ASTM Data
Izod Impact, Notched 2.94 J/cm
5.51 ft-lb/in
ASTM Data
0.690 J/cm

@Temperature -50.0 °C
1.29 ft-lb/in

@Temperature -58.0 °F
ASTM Data
Impact Test 22.0 J

@Temperature -30.0 °C
16.2 ft-lb

@Temperature -22.0 °F
Instrumented Dart Total Energy
39.6 J

@Temperature 23.0 °C
29.2 ft-lb

@Temperature 73.4 °F
Instrumented Dart Total Energy
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 81.0 µm/m-°C

@Temperature 20.0 °C
45.0 µin/in-°F

@Temperature 68.0 °F
ASTM data
Specific Heat Capacity 2.16 J/g-°C
0.516 BTU/lb-°F
Thermal Conductivity 0.181 W/m-K
1.26 BTU-in/hr-ft²-°F
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C
185 °F
Unannealed; ASTM Data
96.0 °C
205 °F
Annealed; ASTM Data
Deflection Temperature at 1.8 MPa (264 psi) 74.0 °C
165 °F
Unannealed; ASTM Data
93.0 °C
199 °F
Annealed; ASTM Data
Vicat Softening Point 101 °C
214 °F
Flammability, UL94 HB

@Thickness 1.47 mm
HB

@Thickness 0.0579 in
Optical Properties Metric English Comments
Gloss 85 %
85 %
Gardner Gloss, 60°