- Solvay Specialty Polymers Solef® 41308 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
Solvay Specialty Polymers Solef® 41308 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 41308 Polyvinylidene Fluoride (PVDF)
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 41308/0001 PVDF is specifically developed for coextrusion.Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec |
<= 0.040 % @Temperature 73.4 °F, Time 24.0 hour |
Method 1; ISO 62 |
| Melt Flow | 6.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| 18 - 24 g/10 min @Load 5.00 kg, Temperature 230 °C |
18 - 24 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa @Temperature 23.0 °C |
4350 psi @Temperature 73.4 °F |
50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 48.0 MPa @Temperature 23.0 °C |
6960 psi @Temperature 73.4 °F |
50 mm/min; ASTM D638 |
| Elongation at Yield | 7.0 % @Temperature 23.0 °C |
7.0 % @Temperature 73.4 °F |
50 mm/min; ASTM D638 |
| Tensile Modulus | 1.90 GPa @Temperature 23.0 °C |
276 ksi @Temperature 73.4 °F |
1.0 mm/min; ASTM D638 |
| Charpy Impact, Notched | 0.850 J/cm² | 4.04 ft-lb/in² | 4 mm thick, 2 m/s; ASTM D256 |
| Coefficient of Friction, Dynamic | 0.31 | 0.31 | vs. Itself; ASTM D1894 |
| Coefficient of Friction, Static | 0.32 | 0.32 | vs. Itself; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 8.0 @Load 1.00 kg |
8.0 @Load 2.20 lb |
CS-10 Wheel; ISO 5470-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 51.6 J/g | 22.2 BTU/lb | Crystallization Heat; ASTM D3418 |
| 52.7 J/g | 22.7 BTU/lb | 80°C to end of melting; ASTM D3418 | |
| Melting Point | 169 °C | 336 °F | ASTM D3418 |
| Crystallization Temperature | 136 °C | 277 °F | Peak, DSC; ASTM D3418 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Generic | PVDF | |
| Processing Method | Coextrusion |
Users viewing this material also viewed the following:
- Poco Graphite SUPERSiC® 3CX Silicon Carbide
- Pyrotek Z-6W Fabric
- Premix Premi-Glas® 8102-13 Glass Reinforced Polyester BMC (discontinued **)
- LyondellBasell Alathon® M6138 High Density Polyethylene
- Sylvin Technologies 9077-75 Natural PVC for Injection Molding
- Taiwan Sheen Soon Sheenthane® AH-592 TPU for Hotmelt Adhesive
- Styron EMERGEâ„¢ 4702-8 Polycarbonate
- A. Schulman POLYFORT™ FXP 1227U UV Stable Copolymer Polypropylene
- Epoxy Technology EPO-TEK® H61 Unfilled Epoxy Adhesive
- Adell BD-10 Nylon 6, Ultra High Impact
Copyright © lookpolymers.com All Rights Reserved