| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers TR 5000 AS/P.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Transparent ABS, Antistatic GradeInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 2.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Yield | 50.8 MPa | 7370 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.76 GPa | 400 ksi | Procedure B, Test Method I(chs 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm | 2.30 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 82.8 °C | 181 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 1.00e+11 ohm-cm | <= 1.00e+11 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.00e+11 ohm | 1.00e+11 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 190 - 250 °C | 374 - 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ GA-1046HLF PVC Compound
- Teknor Apex APEX® 3707-70LG-NT Polyvinyl Chloride, Flexible
- SK Chemicals SKYTHANE® S168D Polyester Based Thermoplastic Polyurethane Elastomer
- Saint-Gobain CHR® 2045-5 Skived PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- Universal Wire Works BAg-1 (AMS 4769) Silver Brazing Filler Metal
- A. Schulman POLYBATCH™ Grey 8899 Concentrate Based In Polyethylene
- ChevronTexaco Delo® 100 Motor Oil, SAE 50
- Caplinq LINQSTAT™ VCF-40012T/2
- SK Chemicals SKYTHANE® 400 Hotmelt Grade UB Polyurethane
Copyright © lookpolymers.com All Rights Reserved