SABIC Innovative Plastics LNP THERMOCOMP RX05494 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RX05494 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RX05494 is a compound based on Nylon 6/6 resin containing glass fiber fillers. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| 0.630 % | 0.630 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 213 MPa | 30900 psi | Type I, 5 mm/min; ASTM D638 |
| 214 MPa | 31000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 29.11 GPa | 4222 ksi | 50 mm/min; ASTM D638 |
| 30.08 GPa | 4363 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 232 MPa | 33600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 315 MPa | 45700 psi | ISO 178 | |
| Flexural Modulus | 6.27 GPa | 909 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 13.02 GPa | 1888 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.39 J/cm | 2.60 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.55 J/cm | 27.26 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 97.0 kJ/m² | 46.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Prodways PLASTCure Model 200 3D Printing Polymer
- North Wood Plastics 60 PP + UNIFILL (40% Wood Fiber)
- PolyOne Geon™ Vinyl Flexible 90253 Polyvinyl Chloride, Flexible (PVC, Flexible)
- RheTech Products HP511-00 27% Talc Reinforced Polypropylene Copolymer, High Performance, Non-UV Stabilized, Natural
- Sylvin Technologies 8600-60 Clear PVC Extrusion Compound
- Videolar 825 E High Impact Polystyrene (HIPS)
- Eastman Tenite 307A4000015 Propionate Clear, Trsp
- 3M 3369 General Purpose Aluminum Foil Tape
- DuPont Performance Polymers Zytel® FG408L NC010 Nylon 66 (Unverified Data**)
- Borealis MB350WG Polypropylene Compound, Mineral Filled
Copyright © lookpolymers.com All Rights Reserved