Diamond Polymers ABS 3501 SHF
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS 3501 SHF.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Super High FlowInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 3.5 - 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.5 - 6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 9.0 - 13 g/10 min @Load 3.80 kg, Temperature 230 °C |
9.0 - 13 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Yield | 36.5 MPa | 5300 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.28 GPa | 330 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
5.00 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 72.8 °C | 163 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Vicat Softening Point | 97.2 °C | 207 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 180 - 250 °C | 356 - 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.14 - 7.58 MPa | 600 - 1100 psi |
Users viewing this material also viewed the following:
- MV Labs RU490 [Ru(C10H8N2)3]Cl2·6H2O Tris(2,2'-bipyridyl)dichlororuthenium(II) dichloride hexahydrate
- Potters Industries Conduct-O-Fil® S4000-S3 Silver-Coated Solid Glass Spheres
- Polymer Resources PPX-G30 Modified-PPO, 30% Glass Reinforced
- Plansee MHC Molybdenum-Hafnium-Carbon
- Overview of materials for Polystyrene, Molded, Unreinforced
- Greene Tweed CHEMRAZ® 585 Perfluoroelastomer
- Momentive Performance Materials "PG" Pyrolytic Graphite
- Westlake 1230S PVC
- ExxonMobil SpectraSyn™ 8 Polyalphaolefin (PAO) Fluid
- Beijing Chemical Industry KAIFA® MN301-G30 Nylon 66 Resin
Copyright © lookpolymers.com All Rights Reserved