Zircar Ceramics ECO-1200B Alumina-Silica Insulation

Category	Ceramic , Oxide , Aluminum Oxide , Silicon Oxide
Manufacturer	Zircar Ceramics
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zircar Ceramics ECO-1200B Alumina-Silica Insulation.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This utility grade board is produced with or without organic binder. Useful to temperatures of 1260°C (2300°F) ECO-1200 is part of hundreds of different thermal process systems. Information provided by Zircar Ceramics.

Physical Properties	Metric	English	Comments
Bulk Density	0.300 g/cc	0.0108 lb/in³
Loss On Ignition	0.00 %	0.00 %

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.000230 GPa	0.0334 ksi	As Received, Parallel to thickness
	0.000230 GPa @Temperature 760 °C, Time 86400 sec	0.0334 ksi @Temperature 1400 °F, Time 24.0 hour	Parallel to Thickness
Compressive Yield Strength	0.0700 MPa	10.2 psi	at 10% Compression, Parallel to thickness

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0550 W/m-K @Temperature 200 °C	0.382 BTU-in/hr-ft²-°F @Temperature 392 °F	Parallel to Thickness
	0.110 W/m-K @Temperature 600 °C	0.763 BTU-in/hr-ft²-°F @Temperature 1110 °F
	0.205 W/m-K @Temperature 1000 °C	1.42 BTU-in/hr-ft²-°F @Temperature 1830 °F	Parallel to Thickness
Maximum Service Temperature, Air	1200 °C	2190 °F
Shrinkage	0.500 % @Temperature 760 °C, Time 86400 sec	0.500 % @Temperature 1400 °F, Time 24.0 hour	Perpendicular to Thickness
	2.50 % @Temperature 1000 °C, Time 86400 sec	2.50 % @Temperature 1830 °F, Time 24.0 hour	Parallel to Thickness
	3.50 % @Temperature 1000 °C, Time 86400 sec	3.50 % @Temperature 1830 °F, Time 24.0 hour	Perpendicular to Thickness

Component Elements Properties	Metric	English	Comments
Al2O3	35 %	35 %
SiO2	64 %	64 %

Electrical Properties	Metric	English	Comments
Dielectric Strength	1.06 kV/mm	27.0 kV/in

Descriptive Properties	Value	Comments
Color	White