DSM Stanyl® TW271F6J10 (PA46+PTFE)-GF30
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Glass Fiber Reinforced |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Stanyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Stanyl® TW271F6J10 (PA46+PTFE)-GF30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced, Heat Stabilized, Wear and Friction Modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | dry; ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 105 MPa | 15200 psi | cond; ISO 527-1/-2 |
| 190 MPa | 27600 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.2 % | 3.2 % | dry; ISO 527-1/-2 |
| 6.0 % | 6.0 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 6.00 GPa | 870 ksi | cond; ISO 527-1/-2 |
| 10.0 GPa | 1450 ksi | dry; ISO 527-1/-2 | |
| Flexural Modulus | 8.50 GPa | 1230 ksi | dry; ISO 178 |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA |
| 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 1.25 J/cm² @Temperature 23.0 °C |
5.95 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 177 °C | 351 °F | 5000 hours Thermal Index; IEC 60216/ISO 527-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
dry; IEC 60695-11-10 |
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
dry; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | cond; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Comparative Tracking Index | 400 V | 400 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- Ritelok PS65 General Purpose Pipe Sealant
- Pasargad Polymer Peyvand Pasamid 3P-H1000W Nylon 6
- Premix Thermoplastics PRE-ELEC® 12-033 (discontinued **)
- Lucas-Milhaupt BRAZE 403 Carbide Brazing Alloy
- DSM Akulon® K224-G6 Nylon 6-30% Glass Reinforced (European and Asian Grade) (Cond)
- Eurofoam Evacell XM 2001 EVA + PE Foam
- Chosun Refractories ALB-65I Special Casting Block
- Conforma Clad WC 210 Tungsten Carbide-Nickel Cladding
- 3D Systems Accura® accuGen™ HC and Ar Plastic for the SLA® 500 System
- Arlon 25122R060 0.060" (1.52 mm) Silicone Rubber on Laminated Fluoropolymer Film
Copyright © lookpolymers.com All Rights Reserved