DSM Novamid® 1017GH33 BK701 PA6-GF33
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 1017GH33 BK701 PA6-GF33.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
33% Glass Reinforced, Heat Stabilized, Injection Molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.30 % | 2.30 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | cond; ISO 527-1/-2 |
| 175 MPa | 25400 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.9 % | 2.9 % | dry; ISO 527-1/-2 |
| 4.5 % | 4.5 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 6.00 GPa | 870 ksi | cond; ISO 527-1/-2 |
| 10.2 GPa | 1480 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 175 MPa | 25400 psi | cond; ISO 178 |
| 280 MPa | 40600 psi | dry; ISO 178 | |
| Flexural Modulus | 5.70 GPa | 827 ksi | cond; ISO 178 |
| 9.20 GPa | 1330 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 8.30 J/cm² @Temperature 23.0 °C |
39.5 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 9.40 J/cm² @Temperature 23.0 °C |
44.7 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 2.60 J/cm² @Temperature 23.0 °C |
12.4 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | dry; ISO 75-1/-2 |
Users viewing this material also viewed the following:
- Huntsman KRYSTALFLEX® PE 193 Polyurethane Optical Aliphatic Film
- Kareline Oy PPMS5050 Natural Fiber Reinforced Polypropylene for injection molding
- SMAC CABLE® 2521S-20-08 Damping Material
- A. Schulman FORMION™ FI 226 40% Glass Fiber Reinforced Ionomer / Nylon Alloy
- API Megol AM DP2433/50PBT SEBS Adhesion Modified Overmolding for Polyesters
Copyright © lookpolymers.com All Rights Reserved