Chi Mei Wonderloy® PC-540 PC/ABS Alloy - Flame Retardant

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Chi Mei Corporation (ChiMei)
Trade Name Wonderloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chi Mei Wonderloy® PC-540 PC/ABS Alloy - Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Heat
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Melt Flow 23.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 23.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 Melt Volume Rate (ml/10 min); ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
50 mm/min; ISO 527
Tensile Strength, Yield 64.0 MPa
9280 psi
50 mm/min; ISO 527
Elongation at Break 95 %
95 %
50 mm/min; ISO 527
Flexural Strength 98.0 MPa
14200 psi
2 mm/min; ISO 178
Flexural Modulus 2.50 GPa
363 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 43.0 kJ/m²
20.5 ft-lb/in²
ISO 180/4A
Charpy Impact, Notched 2.50 J/cm²
11.9 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
annealed; ISO 75
96.0 °C
205 °F
unannealed; ISO 75
Vicat Softening Point 99.0 °C

@Load 5.00 kg
 210 °F

@Load 11.0 lb
 50°C/hr; ISO 306
106 °C

@Load 1.00 kg
 223 °F

@Load 2.20 lb
 50°C/hr; ISO 306
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0590 in