LATI Laramid G/30 PPA, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer LATI
Trade Name Laramid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laramid G/30 PPA, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.0105 cm/cm
0.0075 - 0.0105 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa

@Temperature 150 °C
 10200 psi

@Temperature 302 °F
100 MPa

@Temperature 120 °C
 14500 psi

@Temperature 248 °F
120 MPa

@Temperature 90.0 °C
 17400 psi

@Temperature 194 °F
150 MPa

@Temperature 60.0 °C
 21800 psi

@Temperature 140 °F
200 MPa

@Temperature 23.0 °C
 29000 psi

@Temperature 73.4 °F
Elongation at Break 3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
3.5 %

@Temperature 60.0 °C
 3.5 %

@Temperature 140 °F
4.4 %

@Temperature 90.0 °C
 4.4 %

@Temperature 194 °F
7.3 %

@Temperature 120 °C
 7.3 %

@Temperature 248 °F
9.0 %

@Temperature 150 °C
 9.0 %

@Temperature 302 °F
Tensile Modulus 5.00 GPa

@Temperature 150 °C
 725 ksi

@Temperature 302 °F
5.50 GPa

@Temperature 120 °C
 798 ksi

@Temperature 248 °F
6.00 GPa

@Temperature 90.0 °C
 870 ksi

@Temperature 194 °F
8.50 GPa

@Temperature 60.0 °C
 1230 ksi

@Temperature 140 °F
12.0 GPa

@Temperature 23.0 °C
 1740 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 140 °C
284 °F
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Vicat Softening Point 270 °C

@Load 5.00 kg
 518 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 310 - 330 °C
590 - 626 °F
Mold Temperature 150 - 170 °C
302 - 338 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
 248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa