Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
Manufacturer | DSM Engineering Plastics |
Trade Name | Akulon® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | DSM Akulon® K224-HG6 (Dry) 30% Glass Reinforced Nylon 6 (North America).pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
Water Absorption | 6.3 % | 6.3 % | Sim. to ISO 62 |
Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | Humidity Absorption; Sim. to ISO 62 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 185 MPa | 26800 psi | ISO 527-1/-2 |
Elongation at Break | 3.5 % | 3.5 % | ISO 527-1/-2 |
Tensile Modulus | 9.50 GPa | 1380 ksi | ISO 527-1/-2 |
Charpy Impact Unnotched | 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
Charpy Impact, Notched | 1.10 J/cm² @Temperature -30.0 °C |
5.24 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
UL RTI, Electrical | 140 °C @Thickness 1.50 mm |
284 °F @Thickness 0.0591 in |
UL746B |
140 °C @Thickness 0.750 mm |
284 °F @Thickness 0.0295 in |
UL746B | |
UL RTI, Mechanical with Impact | 120 °C @Thickness 0.750 mm |
248 °F @Thickness 0.0295 in |
UL746B |
125 °C @Thickness 1.50 mm |
257 °F @Thickness 0.0591 in |
UL746B | |
UL RTI, Mechanical without Impact | 140 °C @Thickness 0.750 mm |
284 °F @Thickness 0.0295 in |
UL746B |
150 °C @Thickness 1.50 mm |
302 °F @Thickness 0.0591 in |
UL746B | |
Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 |
HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
Dielectric Constant | 3.3 @Frequency 1e+6 Hz |
3.3 @Frequency 1e+6 Hz |
IEC 60250 |
3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
IEC 60250 | |
Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
IEC 60250 |
0.015 @Frequency 1e+6 Hz |
0.015 @Frequency 1e+6 Hz |
IEC 60250 | |
Comparative Tracking Index | 400 - 599 V | 400 - 599 V | PLC 1; UL 746A |
500 V | 500 V | IEC 60112 |
Descriptive Properties | Value | Comments |
---|---|---|
Heat stabilized or stable to heat | Yes | |
Injection molding | Yes | |
Release Agent | Yes | |
With Fillers | Yes |