DSM Akulon® K223-KM6 Nylon 6-30% Mineral Reinforced (European Grade) (Dry) (discontinued **)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DSM Akulon® K223-KM6 Nylon 6-30% Mineral Reinforced (European Grade) (Dry) (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier film, stock shapes, convoluted tubes, and monofilament. Akulon XP is a high-productivity, high-performance PA6 grade for film extrusion processes. Medium viscosity, unreinforced or reinforced Akulon grades are used for various injection molding and blow molding applications. Akulon® Ultraflow® is a high-productivity, high-performance PA6 family for molding processes.Key applications for Akulon: Automotive: Intake manifold, Engine, Powertrain, Airbag containers, Exterior trim, Interior trim, Electrical components and connectorsConsumer durables: Power tools, Lawn and garden tools, Small appliances, Sports and leisure equipment, Furniture, Industrial Goods, TransportationE&E: Low voltage switch gear/power distribution, Lighting, Power connectorsFilm: Specialty and barrier filmsInformation provided by DSM.

Physical Properties	Metric	English	Comments
Density	1.36 g/cc	0.0491 lb/in³	ISO 1183
Water Absorption	7.0 %	7.0 %	Sim. to ISO 62
Moisture Absorption at Equilibrium	2.2 %	2.2 %	Humidity Absorption; Sim. to ISO 62
Linear Mold Shrinkage, Flow	0.011 cm/cm	0.011 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.011 cm/cm	0.011 in/in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527-1/-2
Elongation at Break	15 %	15 %	ISO 527-1/-2
Tensile Modulus	5.00 GPa	725 ksi	ISO 527-1/-2
Charpy Impact Unnotched	12.0 J/cm² @Temperature -30.0 °C	57.1 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	19.0 J/cm² @Temperature 23.0 °C	90.4 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.550 J/cm² @Temperature -30.0 °C	2.62 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.800 J/cm² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	40.0 µm/m-°C @Temperature 20.0 °C	22.2 µin/in-°F @Temperature 68.0 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	40.0 µm/m-°C @Temperature 20.0 °C	22.2 µin/in-°F @Temperature 68.0 °F	ISO 11359-1/-2
Melting Point	220 °C	428 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	190 °C	374 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	85.0 °C	185 °F	ISO 75-1/-2
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	IEC 60695-11-10

Descriptive Properties	Value	Comments
Heat stabilized or stable to heat	Yes
Injection molding	Yes
Release Agent	Yes
With Fillers	Yes