SABIC Innovative Plastics LNP FARADEX PS003E PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP FARADEX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP FARADEX PS003E PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* FARADEX* PS003E is a compound based on Nylon 6 resin containing 15% Stainless Steel. Added features of this material include: EMI/RFI Shielding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | |
| Moisture Absorption | 1.30 % | 1.30 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0072 cm/cm @Time 86400 sec |
0.0072 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527 |
| 55.0 MPa | 7980 psi | ASTM D638 | |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | ISO 527 |
| 55.0 MPa | 7980 psi | ASTM D638 | |
| Elongation at Break | 8.6 % | 8.6 % | ISO 527 |
| 23 % | 23 % | ASTM D638 | |
| Elongation at Yield | 3.3 % | 3.3 % | ISO 527 |
| 9.6 % | 9.6 % | ASTM D638 | |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527 |
| 3.15 GPa | 457 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 81.0 MPa | 11700 psi | ISO 178 |
| 82.0 MPa | 11900 psi | ASTM D790 | |
| Flexural Modulus | 2.31 GPa | 335 ksi | ASTM D790 |
| 2.40 GPa | 348 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.89 J/cm | 7.29 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 43.0 kJ/m² | 20.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J | 1.48 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 70.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 42.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 75.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 171 °C | 340 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 186 °C @Thickness 3.20 mm |
367 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 62.0 °C @Thickness 3.20 mm |
144 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | ASTM D257 |
| Surface Resistance | 1000 ohm | 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE HJ753 Thermoplastic Elastomer, PP/Elastomer, Mineral Reinforced
- Gouda Vuurvast LP 60 AAP Dense Refractory Brick
- Techmer ES Plaslube® J-4/35/TF/15 NAT PA6/12
- SABIC Innovative Plastics LNP LUBRICOMP KFI12 Acetal Copolymer
- SABIC Innovative Plastics LNP THERMOTUF DF008EI PC
- Eurostar Staramide RB008 PA66, 40% Glass Bead Filled, Injection Molded
- Applied Composites 175 Vinylester SMC
Copyright © lookpolymers.com All Rights Reserved