SABIC Innovative Plastics LNP Verton WV007XXP PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Verton WV007XXP PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP VERTON* WV007XXP is a compound based on Polybutylene Terephalate resin containing Long Glass.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 |
| 1.59 g/cc | 0.0574 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0021 - 0.0055 cm/cm @Time 86400 sec |
0.0021 - 0.0055 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0090 cm/cm @Time 86400 sec |
0.0050 - 0.0090 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0055 - 0.0093 cm/cm @Time 86400 sec |
0.0055 - 0.0093 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 141 MPa | 20500 psi | ISO 527 |
| 146 MPa | 21200 psi | ASTM D 638 | |
| Elongation at Break | 1.3 % | 1.3 % | ISO 527 |
| 1.4 % | 1.4 % | ASTM D 638 | |
| Tensile Modulus | 13.44 GPa | 1949 ksi | 1 mm/min; ISO 527 |
| 14.0 GPa | 2030 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
| 213 MPa | 30900 psi | ASTM D 790 | |
| Flexural Modulus | 10.39 GPa | 1507 ksi | ASTM D 790 |
| 11.23 GPa | 1629 ksi | ISO 178 | |
| Izod Impact, Notched | 2.78 J/cm @Temperature 23.0 °C |
5.21 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 7.05 J/cm @Temperature 23.0 °C |
13.2 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 27.0 kJ/m² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² @Temperature 23.0 °C |
17.6 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 9.00 J | 6.64 ft-lb | Multiaxial Impact; ISO 6603 |
| 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 36.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 64.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 231 °C | 448 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 222 °C @Thickness 3.20 mm |
432 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ HPP GRMF30 Homopolymer Polypropylene Glass/Mineral Filled
- Industrial Laminates/Norplex NP511 Glass Fabric
- Techmer ES HiFill® ABS GF10 A1 10% Glass Filled
- Techmer ES HiFill® PA6 0390 S1 BK
- Styron CALIBREâ„¢ 302-10 Polycarbonate Resin
- Polyram PlusTek RA702 Nylon 66 for Injection Molding, UV Stabilized
- Trelleborg B500 Commercial Nitrile Rubber
- ExxonMobil LLDPE LL 8360.29 Linear Low Density Polyethylene Resin
Copyright © lookpolymers.com All Rights Reserved