Multibase C6-540 Dow-Corning Class VI Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Multibase
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase C6-540 Dow-Corning Class VI Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Multibase
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
Relative, no post cure; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 40
40
no post cure; ASTM D2240
42
42
post cured-4 hours at 177°C; ASTM D2240
43
43
post cured-2 hours at 177°C; ASTM D2240
44
44
post cured- 8 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 8.722 MPa
1265 psi
post cured- 4 hours at 177°C; ASTM D412
8.729 MPa
1266 psi
post cured- 2 hours at 177°C; ASTM D412
9.480 MPa
1375 psi
post cured- 8 hours at 177°C; ASTM D412
9.611 MPa
1394 psi
no post cure; ASTM D412
Tensile Strength, Yield 2.12 MPa
308 psi
at 200%, no post cure- press cured for 5 minutes; ASTM D412
2.48 MPa
359 psi
200%, post cured- 4 hours at 177°C; ASTM D412
2.70 MPa
391 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
2.85 MPa
413 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 642 %
642 %
post cured- 2 hours at 177°C; ASTM D412
659 %
659 %
post cured- 4 hours at 177°C; ASTM D412
660 %
660 %
post cured- 8 hours at 177°C; ASTM D412
742 %
742 %
no post cure; ASTM D412
Tear Strength 41.9 kN/m
239 pli
Die B, no post cure; ASTM D624
44.9 kN/m
256 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
45.1 kN/m
257 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
45.8 kN/m
261 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
Compression Set 46 %
46 %
no post cure; ASTM D395
Thermal Properties Metric English Comments
Shrinkage 2.0 %
2.0 %
no post cure