Covestro Makroblend® DP 7645 Polycarbonate + PET, Impact Grade
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Covestro |
| Trade Name | Makroblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Makroblend® DP 7645 Polycarbonate + PET, Impact Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Developmental productISO 7792-PC/PET,MHPR,-020(PC/PET)-blends, impact modifiedInjection molding gradeunreinforcedPreprocessingMax. Water content
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| 1.03 g/cc @Temperature 270 °C |
0.0372 lb/in³ @Temperature 518 °F |
Melt | |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 260 °C |
12 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527-1/-2 |
| Elongation at Break | >= 50 % | >= 50 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527-1/-2 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| Specific Heat Capacity | 1.76 J/g-°C | 0.421 BTU/lb-°F | Melt |
| Thermal Conductivity | 0.165 W/m-K | 1.15 BTU-in/hr-ft²-°F | Melt |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 | |
| Oxygen Index | 20 % | 20 % | ISO 4589-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| 270 °C | 518 °F | Injection Molding; ISO 294 | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| 70.0 °C | 158 °F | Injection Molding; ISO 10724 | |
| Ejection Temperature | 170 °C | 338 °F | |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Asia Pacific | |
| Europe | ||
| India | ||
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| Eff. thermal diffusivity (m²/s) | 9.08E-08 | |
| Feature | Release agent | |
| Form | Pellets | |
| Process | Injection Molding |
Users viewing this material also viewed the following:
- Malvern Minerals Novakup® Daper Surface-Treated Lamellar Quartz Filler/Extender
- Gwent Electronic Materials P2121112P6 Oxygen Plasma Modified Graphene Nanoplatelets
- SABIC Innovative Plastics LNP STAT-LOY A3000TXJ ABS
- A. Schulman FORMION™ FI 234 20% Mineral Reinforced Ionomer / Nylon Alloy
- A. Schulman FORMION™ FI 391E Ionomer
- Hexcel® HexWeb® CRF-3/8-ACG-.003-3.7 Chromate free ACG® Honeycomb
- BASF Procom® T20C 556 Polypropylene
- Mitsubishi Xantar® G8F 23 R Polycarbonate-40% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved